Pharmaceutical composition for oral use with improved absorption

ABSTRACT

The present invention presents a pharmaceutical composition for oral use with improved absorption, which comprises drug, aminoalkyl methacrylate copolymer E, and acidic substance and is obtained by bringing said 3 components together and uniformly mixing at least this polymer and this acidic substance, and a method of improving oral absorption/by using this pharmaceutical composition. Moreover, the present invention presents an agent for improving oral absorption that increases drug permeability of the digestive tract mucous membrane and/or mucous layer present on the surface of this membrane, whose active ingredient is aminoalkyl methacrylate copolymer E. In addition, the present invention presents an oral agent for improving absorption by increasing drug permeability of the digestive tract mucous membrane and/or the mucous layer distributed over this mucous membrane, whose effective component is aminoalkyl methacrylate copolymer E.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Application No.60/218,980, filed Jul. 17, 2000, the disclosure of which is herebyincorporated by reference in its entirety for all purposes.

TECHNICAL FIELD OF THE INVENTION

The present invention pertains to an oral agent for improving absorptionthat enhances drug permeability of the digestive tract mucous membraneand/or mucous layer distributed over this mucous membrane, whoseeffective component is aminoalkyl methacrylate copolymer E, and to useas an oral agent for improving absorption that enhances drugpermeability of the digestive tract mucous membrane and/or mucous layerdistributed over this mucous membrane, whose effective component isaminoalkyl methacrylate copolymer E. Moreover, the present inventionpertains to a pharmaceutical composition for oral use with improvedabsorption comprising aminoalkyl methacrylate copolymer E, which isparticularly suitable for this enhancement of drug permeability of thedigestive tract mucous membrane and/or mucous layer and improvement oforal absorptivity.

BACKGROUND OF THE INVENTION

Drugs that have been administered orally quickly pass through theesophagus to reach the stomach. The stomach walls are made from the 3layers of mucous membrane, muscle layer, and serous membrane. However,in contrast to the small intestine, the effective surface area forabsorption is small, and therefore, with the exception of some drugs,the stomach plays a small role as an absorption site. On the other hand,the small intestine of humans consists of the duodenum, jejunum, andileum. It is the longest of the digestive tract and its effectivesurface area for absorption is large. Therefore, it is the ideal sitefor absorption of many drugs. However, epithelial cells, which have aplasma membrane made from a lipid double layer, cover the surface of thedigestive tract mucous membrane site very closely and therefore,absorption is strongly restricted in the case of drugs that are verywater soluble and polymer drugs. Moreover, in addition to the digestivetract mucous membrane, the mucous layer that ordinarily covers thedigestive tract mucous membrane also becomes a barrier blocking theabsorption of drugs by the digestive tract. Consequently, drugs thathave been orally administered are first absorbed in vivo after passingthrough the above-mentioned two barriers of the mucous layer coveringthe mucous membrane surface and the mucous membrane.

The above-mentioned mucous layer is mainly made from the components of,glycoprotein such as mucin, cholesterol, lipids such as linoleic acid,proteins, DNA, and others, including various metal ions, such as calciumions, etc. Moreover, the mucous membrane also contains traces of metalions, etc. Consequently, drugs that are difficult to absorb through thedigestive tract because of interaction with various biologically-derivedcomponents are present in the mucous layer and/or mucous membrane of thedigestive tract.

For instance, bisphosphonate compounds have (P—C—P) bonds in theirmolecular structure and therefore, as with phosphonate compounds ingeneral, have strong affinity with bivalent metal ions, such as calciumions, etc., and bond with these metal ions to form insoluble complexes.Consequently, when bisphosphonate compounds are taken after eating orsimultaneously with calcium agent, a slightly soluble complex is formedin the digestive tract and therefore, absorptivity of the bisphosphonatecompound in the digestive tract is markedly reduced.

Moreover, it is known that there are cases where digestive tractabsorption is blocked with substances that form complexes of inferiorpermeability of the mucous layer and mucous membrane, such as complexesof drugs and bile acids, etc.

Furthermore, the absorption route, solubility, lipophilicity, molecularweight, decomposition by digestive enzymes etc., of the drug areconsidered to be other factors that block digestive tract absorption.

The drug absorption routes include the route of passage through the cellmembrane of mucous membrane cells and the route of passage throughspaces between cells. In order for a drug to be absorbed, the drug mustdissolve by either route. Consequently, drugs are slightly soluble anddrugs that form an insoluble complex with in vivo components aredifficult to absorb. In the case of the route of passage through thecell membrane, the drug must pass through the lipid membrane of the celland therefore, drugs of low lipophilicity are generally difficult toabsorb.

As explained above, there appear to be various reasons why drugs aredifficult to absorb through the mucous layer and/or mucous membrane ofthe digestive tract.

The fact that drugs have difficulty passing through the mucous layer ofthe digestive tract has been reported many times in the past. Forinstance, J. Karlsson et al. report that the mucous layer accounts for78% of the barrier to absorption of testosterone (Int. J. Pharm., 1993).Moreover, I. W. Kellaway et al. report that the mucous layer reducesbioavailability of tetracycline by 50% (J. Pharm. Pharmacol., 27 (4),pp. 281-283, 1975). Furthermore, A. W. Larhed et al. also report thatthe mucous layer reduces the diffusion coefficient of testosterone by50% (J. Pharm. Sci, 86, pp. 660-665, 1997). In addition, it is reportedthat bisphosphonate compounds form a chelate with calcium ions withinthe digestive tract to produce an insoluble complex and absorption fromthe digestive tract is thereby reduced (Br. J. Cancer, 71, Suppl. 24,67, 1995). It is also reported that the absorption of pafenolol from thesmall intestine was inhibited by interaction with bile acids(Pharmaceutical Research, 10(6): pp. 879-83, 1993).

Consequently, enhancement of in vivo absorption of a drug by preventinginteraction with the mucous layer or a substance present in the mucouslayer or mucous membrane and/or enhancement of digestive tractabsorption of a drug by improving drug permeability through cells and/orspaces between cells when the digestive tract mucous membrane isaffected, targeted at drugs that are difficult to absorb from thedigestive tract due to interaction with the digestive tract mucous layerand/or mucous membrane, including drugs that are difficult to absorbfrom the digestive tract because permeability of the mucous layerpresent on the digestive tract mucous membrane is poor, drugs that forman insoluble complex by interaction with a substance present in themucous layer and are therefore difficult to absorb, drugs that aredifficult to absorb from the digestive tract because of poorpermeability of the mucous membrane of the digestive tract, etc., is animportant technical topic in terms of hoping for satisfactorypharmacological activity from a drug.

On the other hand, the following methods are known as technology forimproving permeability of drugs through the digestive tract mucouslayer:

For instance, K. Morimoto et al., report increasing absorption ofsulfaguanidine, phenol red or scopolamine by the addition hyaluronidase(J. Pharmacobiodyn, 9, No. 6, s-58, 1986), A Wikman et al. reportreducing the mucous layer and improving permeability of testosterone bythe addition of N-acetylcysteine (Pharm. Res., 10, No. 6, pp 843-852,(1993)), H. Asada et al. report improving permeability of the mucouslayer of the duodenum and large intestine by modification of insulinwith caproic acid (J. Pharm. Sci., 84, No. 6, pp. 682-687, 1995), and L.Hovgaard et al. report improving dispersion in the mucous layer byforming a compound of dodecyl maltoside and insulin (J. ControlledRelease, 19, No. 1-3, pp. 99-108, 1992). Nevertheless, these methods aretechnologies for improving drug migration through the mucous layer byreducing the mucous layer or forming a specific drug complex and are notmeans for improving oral absorption by preventing interaction between adrug and components of the mucous layer and mucous membrane.

Furthermore, J. H. Lin et al. report that absorption of alendronate(4-amino-1-hydroxy butylidene 1,1-bisphosphonate), whose absorption isreduced due to the formation of a compound with calcium ions in vivo, isincreased by chelators, such as EDTA, citric acid, etc. (Pharm. Res., 8,No. 10, Suppl., S273, 1991), but this method is simply technology thatdeals with chelators of specific drugs. Moreover, N. G. M. Schipper etal. report that chitosan, which are cationic natural polymers, have drugabsorption-promoting effects as a tight-junction opener of the digestivetract mucous membrane in tests using Caco-2 cells. Nevertheless, it isreported that chitosan reduce drug permeability by interaction with themucous layer in tests using HT-29 cells in vitro, and they do notimprove oral absorption by preventing interaction between a drug andcomponents of the mucous layer and mucous membrane of the digestivetract (Eur. J. Pharm. Sci., 8, No. 4, pp. 335-343, 1999).

On the other hand, aminoalkyl methacrylate copolymer E is a copolymer ofmethyl methacrylate and butyl methacrylate and dimethylaminoethylmethacrylate that was developed by Röhm, and is a polymer substancemarketed under the brand name of Eudragit™ E100 or Eudragit™ EPO (bothby Röhm GmbH).

Aminoalkyl methacrylate copolymer E is a famous film coating base thatis commonly used to mask the bitter taste and color of tablets andgranules and provide moisture resistance, etc., having the properties of(1) quickly dissolving in gastric juices and (2) dissolving in bufferwith a pH of 5.0 or lower and expanding film in buffer at a pH of 5.0 orhigher. Consequently, in addition to masking the bitter taste and colorof drugs and providing moisture resistance, aminoalkyl methacrylatecopolymer E is being used for solubilization of drugs, etc.

Moreover, aminoalkyl methacrylate copolymer E is used as a base thatforms a solid dispersion in order to increase solubility of slightlysoluble drugs.

Nevertheless, the fact that oral absorptivity is improved whenaminoalkyl methacrylate copolymer E enhances permeability of drugs inthe digestive tract mucous membrane and/or mucous layer was not known atall in the past.

In addition, aminoalkyl methacrylate copolymer E is a gastrosolublepolymer base and therefore, it has not been used to make pharmaceuticalpreparations by being mixed with acidic substances, which would degradethis function.

Incidentally, the following methods are known as technology for usingaminoalkyl methacrylate copolymer E to improve oral absorption of drugs:

An invention relating to a solid dispersion consisting of4″-O-paramethoxyphenylacetyl)tyrosine antibiotic and acrylic polymercopolymer, such as aminoalkyl methacrylate copolymer E, etc., isdisclosed in EP 413,299 (corresponds to Japanese Kokai Patent No. Hei3-74396).

Moreover, an invention pertaining to a method of producing a soliddispersion of a slightly soluble drug comprising this drug andaminoalkyl methacrylate copolymer E using a biaxial extruder isdisclosed in U.S. Pat. No. 5,456,923.

Nevertheless, these technologies only increase solubility of a drug andas a result, improve oral absorption by making the above-mentioneddispersion. They do not use the function of aminoalkyl methacrylatecopolymer E of improving digestive tract absorption of drugs in themucous layer and mucous membrane of the digestive tract.

In addition, these patent gazettes do not disclose or suggest technologythat realizes excellent absorption from the mucous layer and mucousmembrane of the digestive tract by uniformly mixing aminoalkylmethacrylate copolymer E and acidic substance.

An invention whereby a core comprising the acid addition salt of a basicdrug is coated by a compound of weak alkalinity to bring pH to theneutral or alkaline region where drug solubility is good and as aresult, bitter taste is improved and drug absorptivity is improved, andaminoalkyl methacrylate copolymer E is used as the coating agent andbinder is disclosed in Japanese Kokai Patent No. Hei 4-327529.

Nevertheless, this technology does not use the function of aminoalkylmethacrylate copolymer E of improving absorptivity from the mucous layerand mucous membrane of the digestive tract.

In addition, this patent gazette dose not disclose technology by whichimprovement to realize excellent absorption from the mucous layer andmucous membrane of the digestive tract by uniformly mixing aminoalkylmethacrylate copolymer E and acidic substance.

DISCLOSURE OF THE INVENTION

As a result of performing intense studies for the purpose of developingoral pharmaceutical preparations of incadronate and minodronic acid,which are known as third-generation bisphosphonates, under this type oftechnical standards, the inventors knew that as with other conventionalbisphosphonates, these bisphosphonate compounds are difficult to absorbthrough the digestive tract. They discovered that the reason for this isthat these compounds and the metal ions contained in food that isconsumed form insoluble complexes, or insoluble complexes are formedwith the mucus components of the digestive tract, particularly bivalentmetal ions such as calcium ions, and as a result, these compounds becomedifficult to absorb through the digestive tract. Therefore, theinventors performed intense research of substances that improveabsorbtivity of bisphosphonate compounds in the mucous layer and as aresult, they found to their complete surprise that the aminoalkylmethacrylate copolymer E used as a film coating base for gastrosolublepolymers or as a polymer base for solid dispersions in conventional oralpharmaceutical preparations will permeate the mucous layer and willpermeate the mucous membrane without forming insoluble complexes whenpresent together with these bisphosphonate compounds in the digestivetract.

As a result of further investigation of the causes of this phenomenon,the inventors further discovered that what is particularly surprising isthat the function of aminoalkyl methacrylate copolymer E as an agent forimproving oral absorption by enhancing drug permeability through thedigestive tract mucous layer and/or mucous membrane is not limited todrugs that are difficult to absorb that form insoluble complexes withbivalent metal ions such as calcium ions, etc., including bisphosphonatecompounds, etc., or that interact with components of the mucous layerand mucous membrane. It also improves absorption of drugs that areordinarily absorbed.

Although the details of the reasons for this phenomenon remain unknown,it appears that by reaching the mucous layer and/or mucous membranebefore permeation of the drug, the aminoalkyl methacrylate copolymer Ein solution form prevents the components contained in these frominteracting with the drug and inhibits the formation of insolublecomplex, or delays the formation of this complex, or the aminoalkylmethacrylate copolymer E reacts directly with the digestive tract mucousmembrane, leading to enhanced drug permeability of the epithelial cellsand/or spaces between cells.

From this viewpoint, the inventors performed further intense studies ofpharmaceutical compositions with which improved absorption in the mucouslayer and/or mucous membrane of the digestive tract can be realized andas a result, discovered that using aminoalkyl methacrylate copolymer E,which thus far has not been used to make pharmaceutical preparations bybeing uniformly mixed with an acidic substance, drug, and acidicsubstance as the essential components of the mixture, it is possible forthese substance to reach the mucous layer and/or mucous membrane of thedigestive tract in solution form by bringing said mixture componentstogether and uniformly mixing preferably these 3 components, or at leastthe aminoalkyl methacrylate copolymer E and acidic substance, and thatoral absorptivity of various drugs is markedly improved.

The present invention was completed based on these discoveries.

That is, the present invention presents

-   -   1. a pharmaceutical composition for oral use with improved        absorption, which comprises drug, aminoalkyl methacrylate        copolymer E, and acidic substance and which is made by bringing        said 3 components together and uniformly mixing at least the        above-mentioned polymer and above-mentioned acidic substance,    -   2. the pharmaceutical composition of above-mentioned 1, wherein        the drug, aminoalkyl methacrylate copolymer E, and acidic        substance are uniformly mixed,    -   3. the pharmaceutical composition of above-mentioned 1 or 2,        wherein the amount of aminoalkyl methacrylate copolymer E that        is added is 0.01 part by weight or more per 1 part by weight of        drug,    -   4. the pharmaceutical composition of any one of above-mentioned        1 through 3, wherein the acidic substance is one where when 1 g        of said substance is dissolved in 50 ml water, pH of said        solution is brought to 6 or lower,    -   5. the pharmaceutical composition of any one of above-mentioned        1 through 4, wherein the amount of acidic substance added is the        amount that will neutralize 10% or more of basic groups of        aminoalkyl methacrylate copolymer E,    -   6. the pharmaceutical composition of any one of above-mentioned        1 through 5, comprising 0.05˜500 parts by weight of aminoalkyl        methacrylate copolymer E per 1 part by weight of drug in the        effective amount for treatment or prevention of disease, and        acidic substance in the amount that will neutralize 10% or more        of the basic groups of the above-mentioned polymer,    -   7. the pharmaceutical composition of any one of above-mentioned        1 through 5, comprising 0.05˜500 parts by weight of aminoalkyl        methacrylate copolymer E per 1 part by weight of drug in the        effective amount for treatment or prevention of disease, and        0.005˜50 parts by weight of acidic substance per 1 part by        weight of the above-mentioned polymer,    -   8. the pharmaceutical composition of any one of above-mentioned        1 through 7, wherein the aminoalkyl methacrylate copolymer E and        acidic substance are granulated,    -   9. the pharmaceutical composition of any one of above-mentioned        1 through 7, wherein the aminoalkyl methacrylate copolymer E and        acidic substance are dissolved in a pharmaceutically acceptable        solvent and/or after dissolution, said substance is spray dried        to obtain a spray-dried substance, or said solution is        lyophilized to obtain a lyophilized substance,    -   10. the pharmaceutical composition of any one of above-mentioned        1 through 7, wherein the aminoalkyl methacrylate copolymer E and        acidic substance are in a state of dissolution and/or suspension        in a pharmaceutically acceptable solvent,    -   11. the pharmaceutical composition of any one of above-mentioned        1 through 10, wherein the form of the pharmaceutical preparation        is 1 or 2 or more selected from the group consisting of        granules, tablets, capsules, and liquid,    -   12. the pharmaceutical composition of any one of above-mentioned        1 through 11, wherein the drug is a drug that is difficult to        absorb,    -   13. the pharmaceutical composition of above-mentioned 12,        wherein the drug is a bisphosphonate compound,    -   14. a method of improving oral absorption of a drug by using a        pharmaceutical composition obtained by bringing drug, aminoalkyl        methacrylate copolymer E, and acidic substance together and        uniformly mixing at least the above-mentioned polymer and acidic        substance,    -   15. the method of above-mentioned 14, wherein a pharmaceutical        composition obtained by uniformly mixing drug, aminoalkyl        methacrylate copolymer E, and acidic substance is used,    -   16. the method of above-mentioned 14 or 15, wherein the        aminoalkyl methacrylate copolymer E is used in the amount of        0.01 parts by weight or more per 1 part by weight of drug,    -   17. the method of any one of above-mentioned 14 through 16,        wherein the acidic substance that is used is one with which when        1 g of said substance is dissolved in 50 ml water, pH of said        solution is brought to 6 or lower,    -   18. the method of any one of above-mentioned 14 through 17,        wherein the acidic substance is used in the amount that will        neutralize 10% or more of the basic groups of aminoalkyl        methacrylate copolymer E,    -   19. the method of any one of above-mentioned 14 through 18,        wherein pharmaceutical composition is used which comprises        0.05˜500 parts by weight of aminoalkyl methacrylate copolymer E        in terms of 1 part by weight of drug in the amount effective to        treat or prevent disease, and acidic substance in an amount that        will neutralize 10% or more of basic groups of the        above-mentioned polymer,    -   20. the method of any one of above-mentioned 14 through 18,        wherein a pharmaceutical composition is used which comprises        0.05˜500 parts by weight of aminoalkyl methacrylate copolymer E        per 1 part by weight of drug in an effective amount for        treatment or prevention of disease, and 0.005˜50 parts by weight        of acidic substance per 1 part by weight of the above-mentioned        polymer,    -   21. the method of any one of above-mentioned 14 through 20,        wherein a composition is used in which the aminoalkyl        methacrylate copolymer E and acidic substance are granulated,    -   22. the method of any one of above-mentioned 14 through 20,        wherein the aminoalkyl methacrylate copolymer E and acidic        substance are dissolved in a pharmaceutically acceptable solvent        and/or used as a spray-dried substance that has been obtained by        spray drying said solution or used as a lyophilized substance        that has been obtained by lyophilization of said solution,    -   23. the method of any one of above-mentioned 14 through 20,        wherein the aminoalkyl methacrylate copolymer E and acidic        substance are used in a state of dissolution and/or suspension        in a pharmaceutically acceptable solvent,    -   24. the method of any one of above-mentioned 14 through 23,        wherein the form of the pharmaceutical preparation is 1 or 2 or        more selected from the group consisting of granules, tablets,        capsules, and liquid,    -   25. the method of any one of above-mentioned 14 through 24,        wherein drug that is difficult to absorb is used as the drug,    -   26. the method of above-mentioned 25, wherein a bisphosphonate        compound is used as the drug,    -   27. an agent for improving oral absorption by increasing drug        permeability of the digestive tract mucous membrane and/or the        mucus layer distributed over this mucous membrane, whose active        ingredient is aminoalkyl methacrylate copolymer E,    -   28. the agent for improving oral absorption of above-mentioned        27 by the effect of inhibiting the formation and/or the effect        of delaying the formation of insoluble complex based on        interaction between the drug and the digestive tract mucous        layer and/or digestive tract mucous membrane,    -   29. the agent that promotes oral absorption of above-mentioned        27 or 28, which is used in the presence of acidic substance,    -   30. the use of aminoalkyl methacrylate copolymer E as an agent        for improving oral absorption that enhances drug permeability of        the digestive tract mucous membrane and/or mucus layer        distributed over this mucous membrane,    -   31. the use of above-mentioned 30, wherein aminoalkyl        methacrylate copolymer E is used as an agent for improving oral        absorption having the effect of inhibiting the formation and/or        the effect of delaying the formation of an insoluble complex        based on the interaction between a drug and the digestive tract        mucous layer and/or digestive tract mucous membrane,    -   32. The use of above-mentioned 31, which is used in the presence        of an acidic substance.

The “digestive tract” in the present specification means the smallintestine consisting of the duodenum, jejunum, and ileum, as well as thelarge intestine consisting of the colon, the ascending colon, transversecolon, descending colon, sigmoid colon, and the rectum.

The term “bring together” in the present specification means the statewhere each component of drug, aminoalkyl methacrylate copolymer E andacidic substance is present close to one another in a solid or liquidstate. Moreover, the general idea of “bring together” also includes thestate where each component contacts one another. Furthermore, there areno special restrictions with respect to the state of the drug, and itcan be used as is or can be pre-treated. When stability drops as aresult of a drug making contact with acidic substance, etc., the drug isused, for instance, in a pre-treated state (for instance, the state ofbeing coated by a water-soluble substance, such as sugar, starch,hydroxypropylmethyl cellulose, etc.), and in this case, the state oftreated drug and above-mentioned components being present close to oneanother or contacting one another is also included in the generalconcept of “bring together.” In addition, “state of being present closeto one another” means that state where each component is present to suchan extent that the purpose of the present invention is realized, makingit possible to improve drug permeability of the digestive tract mucouslayer and/or mucous membrane and improve oral absorption.

The term “at least” in the present specification means the 2 componentsof aminoalkyl methacrylate copolymer E and acidic substance, or the 3components of drug, aminoalkyl methacrylate copolymer E, and acidicsubstance.

The term “uniformly” in the present specification means the state whereeach component of drug, aminoalkyl methacrylate copolymer E, and acidicsubstance is uniformly dispersed and present as a whole, that is, thestate where there is no misdistribution. For instance, the state wherethere is misdistribution of any of the components as in the case of3-layer tablets where drug, aminoalkyl methacrylate copolymer E andacidic substance are each layered, etc., is not included in “uniformly.”Moreover, “uniformly mixed” is the state of being mixed by methods knownin the field of pharmaceutical preparations, and an example is a solidcomposition produced by physical mixing, spray drying, lyophilization,or granulation (wet granulation, dry granulation) of each component, ora liquid composition where each component is suspended and/or dissolvedin a pharmaceutically acceptable solvent, such as water, etc. FIG. 1shows some of the embodiments, but [the present invention] is notlimited to these embodiments.

First, the novel use of the present invention will be described.

The present invention pertains to an agent for improving oral absorptionby enhancing drug permeability in the digestive tract mucous membraneand/or the mucous layer distributed over this mucous membrane whoseeffective component is aminoalkyl methacrylate copolymer E.

The use of the present invention is characterized in that oralabsorption of drugs is improved by the effect of inhibiting reduction ofdrug permeability of the mucous layer, and the effect of inhibitingand/or the effect of delaying the formation of insoluble complex, etc.,based on interaction between components of the mucous layer and/ormucous membrane of the digestive tract and drugs, of aminoalkylmethacrylate copolymer E.

The pharmaceutical composition for oral use with [improved] absorptionof the present invention will now be described:

The pharmaceutical composition of the present invention is characterizedin that aminoalkyl methacrylate copolymer E and acidic substance areuniformly mixed, and in that acidic substance in an amount that willneutralize 10% or more of the basic groups of this polymer is uniformlymixed with this polymer. The pharmaceutical composition that is obtainedby uniformly mixing both substances has advantageous effects in that (1)this polymer can be dissolved, even at neutral sites or sites of weakalkalinity in the digestive tract and therefore, it is possible toimprove absorption of drugs with which in the past there was apparentlya reduction in oral absorption because an insoluble complex (forinstance, complexes based on interaction with each biological componentpresent in the digestive tract, digestive tract mucous layer ordigestive tract mucous membrane) (for example, insoluble complex, suchas a complex based on interaction with metal ions, including calciumions, magnesium ions, etc., or with biologically secreted components,such as bile acids, etc.) is formed inside the digestive tract, (2) theoptimum absorption site generally varies with the type of drug andtherefore, a pharmaceutical preparation design that takes intoconsideration the optimal absorption site is necessary, but aminoalkylmethacrylate copolymer E can be dissolved of course in the smallintestine with a large effective absorption surface area, including theduodenum of the upper small intestine and the jejunum and ileum, etc.,as well as in the colon, including the ascending colon, transversecolon, descending colon, and sigmoid colon, and rectum, etc., of thelower digestive tract with a low water content, and as a result, theentire digestive tract becomes the effective absorption site of thedrug, (3) a reduction in drug permeability of the mucous layer based oninteraction between the components of the mucous layer and/or mucousmembrane of the digestive tract can be inhibited by aminoalkylmethacrylate copolymer E, (4) oral absorption of a drug can be improvedby the effect of inhibiting and/or the effect of delaying the formationof insoluble complex, etc.

There are no particular restrictions to the drug used in the presentinvention as long as it is one used as a pharmaceutically activecomponent for treatment or prevention of disease. Examples of this drugare drugs that are difficult to absorb because of interaction with thedigestive tract mucous layer and/or mucous membrane, such as drugs thatare difficult to absorb from the digestive tract because permeability ofthe mucous layer present on the digestive tract mucous membrane is poor,drugs that are difficult to absorb due to interaction with substancespresent in the mucous layer, drugs that are difficult to absorb becauseof poor permeability of the digestive tract mucous membrane, etc., ordrugs that are difficult to absorb because they form insoluble complexeswith bile acids. Moreover, in addition to the above-mentioned drugs thatare difficult to absorb, the drugs used in the present invention includeall drugs that are normally absorbed. For instance, natural extractsderived from flora and fauna (for instance, extracts, tinctures, etc.),or compounds isolated from extracts, etc., or compound that have beenchemically synthesized, etc., are included in the present invention. Thedrug can be a single component, or it can be a mixture of two or morecomponents. In addition, when the drug is a compound, salts ofcompounds, various solvates of these compounds that are pharmaceuticallyacceptable (for instance, water, etc.), and solvates of salts of thesecompounds are included in the present invention. Moreover, their crystalpolymorphs are also included. When asymmetric carbons are found in thestructure of the compound and there are optical isomers or stereoisomersof the compound, these optical isomers, stereoisomers, and mixtures ofthese isomers are all included in the present invention. There are noparticular restrictions to the salt of the compound as long as it is onethat is pharmaceutically acceptable. Specific examples are mineral acidsalts of hydrochlorides, hydrobromides, hydroiodides, phosphates,nitrates, sulfates, etc., organic sulfonates, such as methanesulfonates,ethanesulfonates, 2-hydroxyethanesulfonates, p-toluenesulfonates, etc.,organic carboxylates, such as acetates, propionates, oxalates,malonates, succinates, glutarates, adipates, tartrates, maleates,malates, mandelates, etc., and the like.

The drug used in the present invention can be an osteoporosis drug, abone metabolism-improving agent, a hypnotic sedative, a sleep-inducingagent, an anti-anxiety agent, an anti-epilepsy agent, an antidepressant,an anti-Parkinson's agent, an agent used for the treatment ofpsychoneurosis, an agent used for the treatment of central nervoussystem disorders, a local anesthetic, a skeletal muscle relaxant, anagent used for the treatment of autonomic nervous system disorders, ananti-inflammatory antipyretic analgesic, a spasmolytic, an anti-vertigoagent, a cardiotonic, an agent for the treatment of arrhythmia, adiuretic, a hypotensive, a vasoconstrictor, a vasodilator, a drug fortreatment of circulatory disorders, an agent for hyperlipidemia, anagent that promotes respiration, an antitussive, an expectorant, anantitussive expectorant, a bronchodilator, an antidiarrheal agent, anagent for controlling intestinal function, an agent for treatment ofpeptic ulcers, a stomachic, an antacid, a laxative, a cholagogue, agastrointestinal drug, an adrenocortical hormone, a hormone, an agentfor treatment of urogenital disorders, a vitamin, a hemostatic, an agentfor treating liver disease, an agent for treatment of gout, an agent fortreatment of diabetes, an antihistamine, an antibiotic, anantibacterial, an anti-malignant tumor agent, a chemotherapeutic agent,a multisymptom cold agent, a nutrition-enhancing health agent, etc.Examples are bisphosphonate compounds (incadronate,((cycloheptylamino)-methylene)bis-phosphonate), YM175; produced by themethod in Japanese Patent No. Hei 7-629 (corresponds to U.S. Pat. No.4,970,335)), minodronic acid([1-hydroxy-2-imidazo(1,2-a)pyridin-3-ylethylidene]bis-phosphonate),YM529; produced by the method entered in Japanese Patent No. Hei6-99457), alendronate (4-amino-1-hydroxybutylidene 1,1-bisphosphonateproduced by the method in U.S. Pat. Nos. 4,922,007, 5,019,651,5,510,517, 5,648,491), ibandronate, etidronate((1-hydroxyethylidene)-1,1-bisphosphonate), olpadronate, chlodronate,zoledronate, tiludronate, neridronate, pomegranate, risedronate,[1-hydroxy-3-(1-pyrrolidinyl)-propylidene]bis-phosphonate, etc.),5-aminosalicylic acid, acyclovir, adinazolam, ascorbic acid, aspirin,acetylsalicylic acid, acetaminophen, acetobutol, acetohexamide,atenolol, atorvastatin, apomorphine, aminopyrine, aminophylline, ethylaminobenzoate, amrinone, amobarbital, albuterol, alprazolam,allopurinal, ampicillin, ambroxole, isoniazide, idebenone, ibuprofen,imipramine, indeloxazine, indomethacin, idenzamide, ethosuccimide,etomidoline, enalapril, ephedrine, erythromycin, oxytetracycline,oxyphenbutazone, osalazine, omeprazole, carmofur, quinidine, quinine,griseofulvin, glibizide, glucagon, glibenclamide, chloramphenicol,chlordiazepoxide, chlorthiazide, ketoconazole, colestimide, codeine,cobamamide, colchicine, zafirlukast, diazepam, digitoxin, diclofenac,diclofenac sodium, cyclophosphamide, digoxin, cycotiamine, dipyridamole,cimetidine, josamycin, sinvastatin, sucralfate, scopolamine,spironolactone, sulpiride, sulfasalazine, sulfadimethoxine,sulfamethizole, sulfaguanidine, sulfamethoxazole, sulfisoxazole,cefotatan, cefuroxime, selegiline, celecoxib, tasosartan, thiotepa,theophylline, dextromethorphan, tetracycline, tepronone, terfenadine,terbutaline, doxorubicin, tramadole, etodolac, triamcinolone,triamterene, torbutamide, nateglinide, nadolol, naproxen, nicotinamide,nitroglycerin, nitrofurantoin, nifedipine, nemonapride, noscapine,hydrocortisone, pafenolol, vardecoxib, sodium valproate, haloperidol,hydrochlorothiazide, hydrocortisone, pilocarpine, faropenem sodium,famotidine, phenacetin, phenyloin, phenylbutazone, phenyl propanolamine,phenobarbital, fenoprofen calcium, pseudoephedrine, budesonide,formoterol fumarate, praunotol, pravastatin, pravastatin sodium,pranrucast, purimidone, fluorouracil, predinisoline, prednisone,procainamide, prostaglandine I derivative, such as beraprost sodium,etc., furosemide, probenecide, bromovaleryl urea, betamethazone,penicillin, peroxetin, perfphenazine, benzyl penicillin, pentazocine,calcium homopanthothenate, polythiazide, chlorophenylamine maleate,midazolam, milnacipran, doxazocin mesilyate, methyl dopa,methylphenidate, methoclopramide, methotrexate, methoprolol, mepirizole,morphine, ranitidine, lamsoprazole, lisinopril, resperidone,riseofulvin, lidocaine, codeine phosphate, dimemorphan phosphate,pyridoxal phosphate, levonorgesterol, reserpine, levo dopa, lovastatin,lorazepam, warfarin, aclarubicin hydrochloride, azasetron hydrochloride,amitriptyline hydrochloride, amosulalol hydrochloride, ampicillinphthalizyl hydrochloride, indenolol hydrochloride, ethambutolhydrochloride, ondansetron hydrochloride, granisetron hydrochloride,chloropromazine hydrochloride, diphenhydramine hydrochloride, dibucainehydrochloride, tamsulasin hydrochloride, thiapride hydrochloride,terazosine hydrochloride, nicardipine hydrochloride, barnidipinehydrochloride, hydralazine hydrochloride, bifemerane hydrochloride,prazosin hydrochloride, propafenone hydrochloride, moperonehydrochloride, ranitidine hydrochloride, ramosetron hydrochloride, butylscopolamine bromide, isosorbid nitrate, quinidine nitrate, guanetidinenitrate, thiamine nitrate, tocopherol acetate, chloral hydrate, etc. Inaddition to bisphosphonate, the “bisphosphonate compounds” in thepresent Specification include bisphosphonic acid, diphosphonate,diphosphonic acid, and their pharmaceutically acceptable salts, as wellas their derivatives. Examples of pharmaceutically acceptable salts are1 or 2 or more selected from the group consisting of alkali metal salts,alkali earth metal salts, ammonium salts, and ammonium salts substitutedby mono-, di-, tri-, or tetra-alkyl (1˜30 carbons). Specific salts arepreferably 1 or 2 or more selected from the group consisting of sodiumsalt, potassium salt, calcium salt, magnesium salt, and ammonium salt.The drug used in the present invention is preferably a bisphosphonatecompound. Of these, incadronate, minodronic acid, alendronate, andethidronate are preferred, and incadronate and minodronic acid areideal.

Peptides, proteins, and their derivatives are also examples of the drugused in the present invention. Examples are insulin, calcitonin,angiotensin, vasopressin, desmopressin, LH-RH (leutinizing hormonereleasing hormone), somostatin, glucagon, oxytocin, gastrin,cyclosporin, somatomedin, secretin, h-ANP (human atrial natriureticpeptide), ACTH (adrenocorticotropic hormone), MSH(melanophore-stimulating hormone), β-endorphin, muramyl dipeptide,enkephalin, neurotensin, bombesin, VIP (vasoactive intestinal peptide),CCK-8 (cholecystokinin-8), PTH (parathyroid hormone), CGRP (calcitoningene-related peptide), TRH (thyrotropin-releasing hormone), encloserin,hGH (human growth hormone), cytokines, such as interleukin, interferon,colony-stimulating factor, tumor necrosis factor, etc., and derivativesof the same, etc. These peptides and proteins include not only thosenaturally derived, but also their pharmacologically active derivativesand their homologs. For instance, natural calcitonin, such as salmoncalcitonin, human calcitonin, pork calcitonin, eel calcitonin, andchicken calcitonin, etc., as well as their homologs, such as theirgenetic recombinants, etc., are included in the calcitonin that is thesubject of the present invention. Moreover, the insulin includes humaninsulin, pork insulin, etc., as well as homologs of the same, such astheir genetic recombinants, etc.

In the case of peptides and proteins, a pharmaceutical preparation fororal use can be presented as long as preparation technology is usedwhereby this drug is delivered to the lower part of the digestive tract,such as the jejunum, ileum, colon, and large intestine, etc., wheredigestive enzymes have little effect without being decomposed. Examplesof this preparation technology are sustained-release pharmaceuticalpreparations (refer to International Publication Pamphlet WO94/06414,for instance), colon-released pharmaceutical preparation (refer toInternational Publication Pamphlet WO95/28963 for instance),timed-release or pulsed-release pharmaceutical preparation (refer to thepost-script of PCT/JP01/03229 (filed on Apr. 16, 2001)/U.S. Ser. No.09/834,410 (filed on Apr. 12, 2001), and International PublicationPamphlet 93-05771, for instance), etc.

As previously mentioned, in addition to drugs that are difficult toabsorb, all drugs that are normally absorbed are included among thedrugs of the present invention. Drugs with which the pharmacologicaleffect in clinical terms is realized by administration of large dosesorally, even though they are difficult to absorb due to interaction withthe digestive tract mucous membrane and/or mucous layer, interactionwith bile acids, etc., are included among drugs that are usuallyabsorbed. The pharmacological effect that is clinically expected can berealized with a smaller dose when the present invention is applied tothese drugs and therefore, a reduction in adverse effects due to thelarge doses administered in the past can be expected.

There are no special restrictions to the amount of drug used in thepresent invention as long as it is the effective amount in terms oftreatment or prevention of disease.

There are no particular restrictions to the state of the aminoalkylmethacrylate copolymer E when it is mixed in the pharmaceuticalcomposition of the present invention as long as it is brought togetherwith the drug and is uniformly mixed with acidic substance, which isdescribed later. This state can be, for instance, a solid, such as apowder of this polymer itself, or a liquid, such as an aqueous solutionof this polymer suspended and/or dissolved in water. Moreover,conventional methods such as crushing, spray drying, lyophilization, wetgranulation, dry granulation, etc., can be used as the method for makinga powder. It is preferred that acidic substance, which is mentionedlater, be added as the dissolution auxiliary agent for this polymer. Theaminoalkyl methacrylate copolymer E can have free amino groups and canbe a soluble salt. The preferred embodiment in the case of soluble saltsis preparation by spray drying or lyophilization of a solution ofaminoalkyl methacrylate copolymer E dissolved, or dissolved andsuspended, together with acid. The aminoalkyl methacrylate copolymer Ecan contain surfactant. There are no special restrictions to thesurfactant that is added as long as it is usually pharmaceuticallyacceptable and it reduces water repellency of this polymer. Nonionicsurfactants (for instance, polyoxyethylene surfactants (such aspolysorbate 80, polyoxil stearate 40, lauroMacrogol,polyoxyethylene-hydrogenated castor oil (HCO-60), sucrose fatty acidester, etc.)), ionic surfactants (anionic surfactants (for instance,sodium laurylsulfate, etc.), cationic surfactants (for instance,benzalconium chloride, etc.), amphoteric surfactants (lecithin, etc.)),etc., are examples. One or a mixture of 2 or more as needed can be used.There are no special restrictions to the amount of surfactant added aslong as it is an amount that will reduce water repellency of thispolymer, but it is usually approximately 0.01˜10 parts by weight,preferably approximately 0.01 to 5 parts by weight, further preferablyapproximately 0.05˜1 part by weight, per 1 part by weight of thispolymer. There are no special restrictions to the solvent in which theaminoalkyl methacrylate copolymer E (containing surfactant when needed)is dissolved or suspended as long as it is a solvent that is usuallypharmaceutically acceptable. Examples are water, organic solvent (forinstance, methanol, ethanol, isopropanol, acetone, etc.), mixtures ofwater and organic solvent, etc. Moreover, the pharmaceutical compositionof the present invention can also contain various fillers that are usedas pharmaceutical additives and other additives. Extenders such aslactose, starch, etc., can also be added as the filler or additive.

There are no special restrictions to the amount of aminoalkylmethacrylate copolymer E used in the present invention as long as therelationship with the amount of drug added is adjusted as needed. It isusually 0.01 part by weight or more, preferably 0.05˜500 parts byweight, further preferably 0.1˜250 parts by weight, particularly 0.5˜50parts by weight, per 1 part by weight of drug. Incidentally, surfactantcan also be mixed with the aminoalkyl methacrylate copolymer E for thepurpose of promoting absorption even further. Nonionic surfactants (forinstance, polyoxyethylene surfactants (such as polysorbate 80, polyoxilstearate 40, lauroMacrogol, polyoxyethylene-hydrogenated castor oil(HCO-60), sucrose fatty acid ester, etc.), ionic surfactants (anionicsurfactants (for instance, sodium laurylsulfate, etc.), cationicsurfactants (for instance, benzalconium chloride, etc.), amphotericsurfactants (lecithin, etc.)), etc., are examples. One or a mixture of 2or more as needed can be used.

There are no special restrictions to the acidic substance used in thepresent invention as long as it is pharmaceutically acceptable andcapable of dissolving the aminoalkyl methacrylate copolymer E byneutralizing some or all of the basic groups of this polymer in thepresence of water. An inorganic acid and/or organic acid with which pHof a solution of 1 g of this acidic substance dissolved or dispersed in50 ml of water is 6 or less is preferred as this acidic substance.Examples of the acidic substance used in the present invention areinorganic acids, such as hydrochloric acid, phosphoric acid, potassiumdihydrogen phosphate, sodium dihydrogen phosphate, etc., organic acidssuch as citric acid, lactic acid, tartaric acid, fumaric acid, phthalicacid, acetic acid, oxalic acid, malonic acid, adipic acid, phytic acid,succinic acid, glutaric acid, maleic acid, malic acid, mandelic acid,ascorbic acid, benzoic acid, methanesulfonic acid, capric acid, capronicacid, caprylic acid, lauric acid, arachidonic acid, erucic acid,linoleic acid, linolenic acid, oleic acid, palmitic acid, myristic acid,stearic acid, etc.; aspartic acid, L-glutamic acid, L-cystein, argininehydrochloride, lysine hydrochloride, L-glutamic acid hydrochloric acidsalt, etc. One or a combination of 2 or more of these can be used.

There are no special restrictions to the amount of acidic substance usedin the present invention as long as it is an amount capable ofdissolving the aminoalkyl methacrylate copolymer E by neutralizing someor all of the basic groups of this polymer in the presence of water. Theamount of this substance that is added is the amount that willneutralize usually approximately 10% or more, preferably approximately15% or more, further preferably approximately 30% or more, particularlyapproximately 40% or more, ideally 50% or more, of the basic groups ofthis polymer. The presence of 50% or more acidic substance is idealbecause the spray-dried product can be easily handled during productionwithout any aggregation, even when stored for a long period of time. Theamount of this acidic substance is adjusted as needed taking intoconsideration solubility and/or acidity of this substance, but it isusually 0.005˜50 parts by weight, preferably 0.01˜30 parts by weight,particularly 0.03˜10 parts by weight, per 1 part by weight aminoalkylmethacrylate copolymer E. Furthermore, when 312.5 g of 1 molahydrochloric acid per 500 g Eudragit E, for instance, is added as theacidic substance used in the present invention and spray dried,calculation can be by the following formula (I): $\begin{matrix}{{\frac{1{x312}{.5}}{1000}\begin{matrix}\left( {{Number}\quad{of}\quad{moles}\quad{of}} \right. \\\left. {{hydrochloric}\quad{acid}} \right)\end{matrix}} = {\frac{X}{{KOH}(56)}\begin{matrix}{{{Number}\quad{of}}\quad} \\\left. {{moles}\quad{of}\quad{KOH}} \right)\end{matrix}}} & {{Formula}\quad(I)}\end{matrix}$

-   -   X=17.49 g, but because it is the amount in 500 g, divide by 500.    -   X/1 g Eudragit E=35 mg KOH

Actually, since the alkali value in 1 g Eudragit E is 163-198 mg KOH,the amount of acid added at this time was 15˜20% the amount that wouldneutralize all of the alkali.

There are no particular restrictions to the uniform mixing of theaminoalkyl methacrylate copolymer E and acidic substance used in thepresent invention as long as it is a state wherein they are broughttogether with the drug and uniformly mixed and the embodiment can beused whereby aminoalkyl methacrylate copolymer E can be dissolved byacidic substance in the presence of water. A state wherein drug, thispolymer and this acidic substance are uniformly mixed is preferred. Theembodiment whereby they are mixed by conventional methods is an exampleof this state. For instance, the embodiment whereby aminoalkylmethacrylate copolymer E prepared by the method described previously bymixing the above-mentioned aminoalkyl methacrylate copolymer E, orliquid of aminoalkyl methacrylate copolymer E and acidic substance, oraminoalkyl methacrylate copolymer E and acidic substance dissolvedand/or suspended in a pharmaceutically acceptable solvent (for instance,water, alcohol (methyl, ethyl, propyl, butyl, etc.) or their mixtures,etc.) together with drug, is made into a powder by conventional methods,such as spray drying, etc., the embodiment whereby aminoalkylmethacrylate copolymer E and acidic substance are mixed by conventionalmethods or are granulated to make a mixture, the embodiment whereby aliquid of aminoalkyl methacrylate copolymer E and acidic substancedissolved and/or suspended in a solvent that is pharmaceuticallyacceptable, the embodiment whereby drug is further added in theabove-mentioned embodiment, etc., are given. There are no particularrestrictions to the pharmaceutical composition that can be specificallyused in these embodiments as long as it is in a form that can be orallyadministered as a pharmaceutical preparation. This preparation can befor instance, a powder, tablets, capsules, a liquid, a suspension, anemulsion, or capsules, etc., filled with a liquid, a suspension, anemulsion, etc.

The method of producing this pharmaceutical preparation can be aconventional method. Specific examples of this preparation aresolution/suspension of aminoalkyl methacrylate copolymer E and acidicsubstance dissolved and/or suspended in pharmaceutically acceptablesolvent, capsules wherein the above-mentioned solution/suspension isfilled in capsules, such as gelatin capsules, mixture obtained by mixingaminoalkyl methacrylate copolymer E and acidic substance by conventionalmethods and then mixing this mixture with drug, granules obtained bymixing aminoalkyl methacrylate copolymer E and acidic substance, addinga solvent that is pharmaceutically acceptable, such as water, etc.,adding a binder such as hydroxypropoyl methyl cellulose, etc., as neededand granulating the product, tablets obtained by mixing pharmaceuticalfiller with the above-mentioned mixture or granulated product and thentableting, capsule preparation of the above-mentioned granules filledin, for instance, gelatin capsules, enteric-coated preparation obtainedby coating the above-mentioned granules with an enteric substance (forinstance, 1:1 copolymer of methyl methacrylate and methacrylic acid(brand name Eudragit™L, Röhm GmbH), 2:1 copolymer of methyl methacrylateand methacrylic acid (brand name Eudragit™S, Röhm GmbH), 1:1 copolymerof ethyl acrylate and methacrylic acid (brand name: Eudragit™ LD-55,Röhm GmbH), hydroxypropyl methyl cellulose phthalate, hydroxypropylmethyl cellulose acetate succinate, carboxymethyl ethyl cellulose,cellulose acetate phthalate, shellac, zein, etc., or enteric-coatedpreparation obtained by coating tablets obtained by tableting theabove-mentioned granules with enteric substance (same as theabove-mentioned). The preparations can be made by conventional methods.In this case, pharmaceutical additives, such as fillers, disintegrators,binders, lubricants, fluidizers, dispersants, suspension agents,emulsifiers, preservatives, stabilizers, etc., can be added to thepharmaceutical composition of the present invention as needed.

The mixture ratio of drug, aminoalkyl methacrylate copolymer E andacidic substance contained in the pharmaceutical composition is 0.05˜500parts by weight (preferably 0.1˜250 parts by weight, further preferably0.5˜50 parts by weight) of aminoalkyl methacrylate copolymer E per 1part by weight drug in the amount effective in terms of treatment orprevention of disease, and the amount of acidic substance that willneutralize 10% or more (preferably 15% or more, further preferably 30%or more, particularly 40% or more, ideally 50% or more) of the basicgroups of the above-mentioned polymer. The mixture ratio can be selectedby using an appropriate combination from the preferred combination ratiofor each component, but of these, the preferred mixture ratio is 0.5˜50parts by weight of aminoalkyl methacrylate copolymer E per 1 part byweight drug in the effective amount in terms of treatment or preventionof disease, and acidic substance in an amount that will neutralize 50%or more of the basic groups of the above-mentioned polymer. Acombination ratio of the above-mentioned 3 components where there are0.05˜500 parts by weight (preferably 0.1˜250 parts by weight, furtherpreferably 0.5˜50 parts by weight) of aminoalkyl methacrylate copolymerE per 1 part by weight drug in the amount that is effective in terms oftreatment or prevention of disease, and 0.005˜50 parts by weight(preferably 0.01˜30 parts by weight, further preferably 0.03˜10 parts byweight) of acidic substance per 1 part by weight of the above-mentionedpolymer in the pharmaceutical composition is also possible. The mixtureratio can be selected by using an appropriate combination from the groupof preferred combination ratios of each component. However, of these,the preferred combination ratio is 0.5˜50 parts by weight of aminoalkylmethacrylate copolymer E per 1 part by weight of drug in an amounteffective for treatment or prevention of disease and 0.03 to 10 parts byweight of acidic substance per 1 part by weight of the above-mentionedpolymer.

The pharmaceutical composition for oral use of improved absorption ofthe present invention can be used in a variety of pharmaceuticalpreparations as previously described. However, further specificpharmaceutical preparations are sustained-released pharmaceuticalpreparations (refer to International Publication Pamphlet WO94/06414,for instance), colon-released pharmaceutical preparations (refer toInternational Publication Pamphlet WO95/28963, for instance),timed-release or pulsed-release pharmaceutical preparation (refer toPCT/JP01/03229 (filed on Apr. 16, 2001), U.S. Ser. No. 09/834,410 (filedon Apr. 12, 2001), International Publication Pamphlet WO93/05771, forinstance), microparticle pharmaceutical preparation (refer to JapaneseDomestic Publication No. Hei 10-511957, for instance), mucous membraneadhesion-type pharmaceutical preparation (refer to Japanese Kokai PatentNo. Hei 5-132416, for instance), etc. The hydrogel-formingsustained-release pharmaceutical preparation described in InternationalPublication WO94/06414, colon-released pharmaceutical preparation (forinstance, a pharmaceutical preparation wherein a mixture of granulationproduct obtained by granulation of the pharmaceutical composition fororal use of improved absorptivity of the present invention andsaccharide that is decomposed by intestinal flora to generate organicacid (for instance, lactulose) is coated with polymer substance that isdissolved by organic acid, then is coated with a nonionic substance,such as hydroxypropyl methyl cellulose as needed, and is further coatedwith enteric substance, or a pharmaceutical preparation wherein tabletsobtained by tableting the above-mentioned mixture are coated withpolymer substance that is dissolved by inorganic acids, are then coatedwith a nonionic substance, such as hydroxypropyl methyl cellulose, etc.,as needed, and further coated by enteric substance) described inWO95/28963, and timed-release pharmaceutical preparation described inabove-mentioned PCT/JP01/03229 (filed on Apr. 16, 2001)/U.S. Ser. No.09/834,410 (filed on Apr. 12, 2001) are preferred.

The timed-release pharmaceutical preparation of PCT/JP01/03229 (filed onApr. 16, 2001)/U.S. Ser. No. 09/834,410 (filed on Apr. 12, 2001) will bedescribed below in detail:

The invention relating to the application in question pertains totimed-release dry-coated tablets, characterized in that they are ahydrogel-forming dry-coated solid pharmaceutical preparation comprisinga core containing the drug and an outer layer made from hydrogel-formingpolymer and hydrophilic base wherein (1) drug and “readily erodiblefiller” are mixed in the core, (2) the percentage erosion of the core isapproximately 40˜approximately 90%, and (3) the outer layer isessentially free of the same drug as the above-mentioned drug.

Determination of Percentage Erosion

Dry-coated tablets containing a drug are moistened for 3 hours in waterat 37° C. and then the gelled part of the tablet is peeled off and thecore that has not eroded is recovered. The core is dried overnight in adryer at 40° C. and weight is determined. Dry weight is subtracted fromthe initial core weight and this is divided by the initial core weight.This value is multiplied by 100 to calculate the percentage erosion (%).

There are no special restrictions to the “readily erodible filler” usedin the core here as long as it is usually pharmaceutically acceptableand it provides a specific percentage erosion as a pharmaceuticalpreparation with the combination of drug and other fillers that is used.This filler can be one that itself quickly dissolves in order to quicklyerode the core and disperse or dissolve the drug component and/or onethat has the ability to quickly dissolve itself and bring pH to one atwhich the drug will readily dissolve. It is preferred that the filler beselected taking into consideration the physicochemical properties of thedrug, particularly whether the drug is an acidic, neutral or basic drug.Examples when the drug is basic are the organic acids of malic acid,citric acid and tartaric acid, and malic acid and citric acid arepreferred. Examples when the drug is neutral or acidic are sucrose,polyethylene glycol, lactulose, etc., and sucrose and polyethyleneglycol are preferred. In this case, 1 or a mixture of 2 or more fillerscan be used. This filler is preferably used as a mixture of 1 or 2 ormore selected from malic acid, citric acid, tartaric acid, sucrose,polyethylene glycol, and lactulose.

The amount of this filler that is added can be adjusted taking intoconsideration the release time that is selected as needed, and isusually approximately 10˜approximately 95 wt %, preferably approximately15˜approximately 80 wt % core tablet. Moreover, it is also possible toadd 1 or 2 or more additives to the core that are pharmaceuticallyacceptable for further increasing the bioavailability of a drug in ordereasily absorb the drug contained in the core, even in the colon wherethe water content is low. Examples of this additive are surfactants,such as polyoxyethylene-hydrogenated castor oil, polyoxyethylenesorbitane higher fatty acid esters, polyoxyethylene polyoxypropyleneglycols, sucrose fatty acid esters, etc. The method of improvement ofthe properties of the drug itself by means described below are alsoeffective. Specific examples are the method whereby a solid dispersionis formed with a water-soluble polymer, such as hydroxypropyl methylcellulose, polyvinyl pyrrolidone, polyethylene glycol, etc., or entericpolymer, such as carboxymethyl ethyl cellulose, hydroxypropyl methylcellulose phthalate, methyl methacrylate-methacrylic acid copolymer, themethod of conversion to a soluble salt, the method of forming aclathrate compound using cyclodextrin, etc. Moreover, 1 or a combinationof 2 or more of these methods can be used, and the above-mentionedadditives and these methods can be combined. It is also possible to coatthe core when necessary. There are no special restrictions to thecoating base used in the present invention as long as it ispharmaceutically acceptable and the purpose of the present invention canbe accomplished, and a polymer base such as hydroxypropyl methylcellulose, etc., is an example. It is also possible to use 1 or asuitable combination of 2 or more appropriate polymer bases.

The hydrogel-forming polymer substance used for the outer layer of thecore here means a hydrogel-forming polymer substance with which thisdry-coated tablet absorbs the water component retained in the upperdigestive tract and gels and is eroded as a result of the contractilemovement of the digestive tract that occurs with the digestion of food,leading to disintegration of the core tablet after a specific amount oftime. Particularly ideal hydrogel-forming polymer substances haveproperties including viscosity during gelling to such an extent thatthey withstand the contractile movement of the digestive tract thataccompanies the digestion of food when they are all but gelled as aresult of this dry coated tablet having absorbed the water retained inthe upper digestive tract and although eroded, move to the lowerdigestive tract retaining their shape to a certain extent and there canbe disintegrated or peeled, etc. For instance, a polymer substancehaving a viscosity of an aqueous 1% solution (25° C.) of 1,000 cps orhigher is preferred. Moreover, the properties of the polymer substancedepend on its molecular weight. Consequently, polymers with a highermolecular weight are preferred as the polymer that forms a hydrogel thatcan be used in this dry-coated tablet. One with a viscosity-averagemolecular weight of 2,000,000 or higher, particularly aviscosity-average molecular weight of 4,000,000 or higher is preferred.Examples of this polymer substance are POLYOX® WSR-303(viscosity-average molecular weight: 7,000,000, viscosity: 7,500-10,000cP (aqueous 1% solution, 25° C.)), POLYOX® WSR Coagulant(viscosity-average molecular weight: 5,000,000, viscosity: 5,500-7,500cP (aqueous 1% solution, 25° C.)), POLYOX® WSR-301 (viscosity-averagemolecular weight: 4,000,000: viscosity: 1,650-5,500 cP (aqueous 1%solution, 25° C.)), and POLYOX® WSRN-60K (viscosity-average molecularweight: 2,000,000, viscosity: 2,000-4,000 cP (aqueous 2% solution, 25°C.)) (all made by Union Carbide), ALKOX® E-75 (viscosity-averagemolecular weight: 2,000,000˜2,500,000, viscosity: 40-70 cP (aqueous 0.5%solution, 25° C.)), ALKOX® E-100 (viscosity average molecular weight:2,500,000˜3,000,000, viscosity: 90-110 cP (aqueous 0.5% solution, 25°C.)), ALKOX® E-130 (viscosity-average molecular weight:3,000,000˜3,500,000, viscosity: 130-140 cP (aqueous 0.5% solution, 25°C.)), ALKOX® E-160 (viscosity-average molecular weight:3,600,000˜4,000,000, viscosity: 150-160 cP (aqueous 0.5% solution, 25°C.)), and ALKOX® E-240 (viscosity-average molecular weight:4,000,000˜5,000,000, viscosity: 200-240 cP (aqueous 0.5% solution, 25°C.)) (all made by Meisei Kagaku Co., Ltd.), PEO-8 (viscosity-averagemolecular weight: 1,700,000˜2,200,000, viscosity: 20-70 cP (aqueous 0.5%solution, 25° C.)), PEO-15 (viscosity-average molecular weight:3,300,000˜3,800,000, viscosity: 130-250 cP (aqueous 0.5% solution, 25°C.), PEO-18 (viscosity-average molecular weight: 4,300,000˜4,800,000,viscosity: 250-480 cp (aqueous 0.5% solution, 25° C.) (all made bySeitetsu Kagaku Co., Ltd.), etc. However, polyethylene oxide with amolecular weight of 2,000,000 or higher is particularly ideal.

The polymer substance of the present invention can be 1 or a combinationof 2 or more with different molecular weights, grades, etc., in order toadjust lag time. Moreover, a mixture with another hydrogel-formingpolymer substance can also be used. In addition, the core can comprisethese hydrogel-forming polymer substances as long as the effects of thetimed-released pharmaceutical preparation of the present invention arenot lost. Sustained release of the drug after lag time is possible whenthe hydrogel-forming polymer substance comprises the core. Theabove-mentioned are also examples of the hydrogel-forming polymersubstance in this case, and polyethylene oxide is preferred.Approximately 10˜approximately 50 wt % of the tablet is preferred as thespecific amount added.

In order for drug release to be possible in the lower digestive tract inhumans, it is necessary to have a gelled outer layer at least 2 hoursafter administration and further, the outer layer must be disintegratedor peeled and the core released when the lower digestive tract isreached. Although it varies with the size of the pharmaceuticalpreparation, the type of polymer substance, the drug and hydrophilicbase, content, etc., the preferred embodiment for forming an outer layerwith this type of property is a pharmaceutical preparation of 600 mg orless per one tablet where the ratio of polymer substance that will forma hydrogel to the entire pharmaceutical preparation is approximately5˜approximately 95%. Approximately 10˜approximately 90 wt % is furtherpreferred. Moreover, it is preferred that the amount of hydrogel-formingpolymer substance added per 1 tablet pharmaceutical preparation beapproximately 20 mg or more per 1 tablet, and approximately 30 mg ormore is further preferred.

Furthermore, when polyethylene oxide is used as the hydrogel-formingpolymer substance, it is preferred that yellow ferric oxide and/or redferric oxide be added as stabilizer to the outer layer of thisdry-coated tablet, or that the dry-coated tablet be coated with these,so that there will be no changes in drug release performance, even ifthe pharmaceutical preparation is stored exposed to light. The yellowferric oxide or red ferric oxide used in the present invention can beused alone or as a mixture.

There are no special restrictions to the mixture ratio of yellow ferricoxide and/or red ferric oxide used at this time as long as it stabilizesthe dry-coated tablet without compromising the timed-release of thepresent invention. This mixture ratio varies with the type and method ofaddition, but when added to the outer layer, approximately1˜approximately 20 wt % is preferred, and approximately 3 toapproximately 15 wt % is further preferred, in terms of the total amountof pharmaceutical preparation. For example, approximately5˜approximately 20 wt % is preferred, and approximately 10˜approximately15 wt % is further preferred, in terms of the entire pharmaceuticalpreparation with red ferric oxide. Approximately 1˜approximately 20 wt %is preferred and approximately 3˜approximately 10 wt % is furtherpreferred with yellow ferric oxide. Approximately 0.3˜approximately 2%is preferred, and approximately 0.5˜approximately 1.5% is furtherpreferred, in terms of tablet weight in the case of coating by filmcoating. Approximately 5˜approximately 50% is preferred andapproximately 10 to approximately 20% is further preferred as theconcentration of yellow ferric oxide or red ferric oxide in the film atthis time. It is preferred that the yellow ferric oxide and/or redferric oxide be uniformly mixed in the outer layer when this ferricoxide is added to the outer layer. Mixing does not necessarily meanphysical mixing. A variety of means, including for instance granulationwith a filler that comprises the outer layer or coating the granulationproduct, etc., can be used. When coated on a dry-coated tablet, it ispossible to dissolve or suspend the above-mentioned ferric oxide in awater-soluble polymer solution, such as hydroxypropyl methyl cellulose,etc., and coat the tablet with a thin film using a film coating device,such as a high coater (Freund Industry Co., Ltd.), etc. One or acombination of 2 or more of these methods can also be used.

The “hydrophilic base” comprising the outer layer of the above-mentioneddry-coated tablet is important in terms of the drug reaching the lowerdigestive tract, where there is little water component, together withwater component and being time-released. This hydrophilic base is onethat can be dissolved before the above-mentioned hydrogel-formingpolymer substance gels. Specifically it is a hydrophilic base with whichthe amount of water needed for dissolution of 1 g of this base is 5 mLor less (20±5° C.), preferably 4 mL or less (same temperature). Examplesof this hydrophilic base are water-soluble polymers, such aspolyethylene glycol (for instance, Macrogol 400, Macrogol 1500, Macrogol4000, Macrogol 6000, Macrogol 20000 (all made by Nihon Yushi)),polyvinyl pyrrolidone (for instance, PVP® K30 (made by BASF)), etc.,sugar alcohols, such as D-sorbitol, xylitol, etc., saccharides, such assucrose, maltose, lactulose, D-fructose, dextran (for instance, Dextran40), glucose, etc., surfactants, such as polyoxyethylene-hydrogenatedcastor oil (for instance, Cremophor® RH40 (BASF), HCO-40, HCO-60 (NikkoChemicals), polyoxyethylene-polyoxypropylene glycol (for instance,Pluronic® F68 (Asahi Denka Kogyo K.K.), etc.), or polyoxyethylenesorbitan fatty acid ester (for instance, Tween 80 (Kanto Kagaku Co.,Ltd.), etc., salts such as sodium chloride, magnesium chloride, etc.,organic acids, such as citric acid, tartaric acid, etc., amino acids,such as glycine, β-alanine, lysine hydrochloride, etc.,aminosaccharides, such as meglumine, etc, and the like. Polyethyleneglycol, sucrose, and lactulose are preferred and polyethylene glycol(particularly Macrogol 6000) is further preferred. Moreover, 1 or acombination of 2 or more hydrophilic bases can also be employed.

When hydrophilic base is added to the above-mentioned dry-coated tablet,the mixture ratio is preferably approximately 5˜approximately 80 wt %per the entire dry-coated tablet, and further, preferably approximately5˜approximately 70 wt % per the entire dry-coated tablet.

The above-mentioned “hydrophilic base” and “readily erodible filler” canalso be selected so that they are the same, but as previously mentioned,the “hydrophilic base” is one with which the amount of water necessaryfor dissolution of 1 g base is 5 mL or less (20±5° C.) and the “readilyerodible filler” is one that shows a result of approximately40˜approximately 90% when the core tablet is analyzed by the method ofdetermining the percentage erosion. Thus, because they are selected inaccordance with their respective definition, the two are differentiatedfrom one another based on the difference in properties in the presentinvention. That is, although one condition of the “readily erodiblefiller” is that it has excellent solubility in water, but anothercondition is that with respect to the correlation between timed releaseof the effective drug and other additives, the filler has the propertyof giving the dry-coated tablet a specific percentage erosion.

With respect to the mixture ratio of outer layer to core here, usuallyapproximately 0.5˜approximately 10 parts by weight is preferred,approximately 1˜approximately 5 parts by weight is further preferred,per 1 part by weight core. Moreover, with respect to the mixture ratioof hydrophilic base and hydrogel-forming polymer substance of the outerlayer, usually approximately 0.1 to approximately 8 parts by weight ispreferred, approximately 0.3-approximately 5 parts by weight is furtherpreferred, per 1 part by weight hydrogel-forming polymer substance.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram showing an embodiment of thepharmaceutical composition of the present invention. FIG. (1-1) is aschematic diagram showing the preparation form (for instance, granules,powders, capsules in which these have been filled, liquid, suspension,emulsion, capsules in which liquid, suspension, emulsion, etc., has beenfilled, etc.) where a layer in which aminoalkyl methacrylate copolymer E(B in the figure) and acidic substance (C in the figure) have beenuniformly mixed is coated on a core comprising drug (A in the figure).FIG. (1-2 a) and FIG. (1-2 b) are schematic diagrams showing the samecomposition, which is an embodiment of the invention of the presentapplication. In the micro view, it is a composition where each componentof drug (A in the figure), aminoalkyl methacrylate copolymer E (B in thefigure), and acidic substance (C in the figure) does not appear to beuniformly dispersed, as shown in FIG. (1-2 a), but the macro view is thecomposition of an embodiment of the invention of the present applicationwhere each component is present uniformly dispersed as a whole, as shownin FIG. (1-2 b). The preparation form in this state is, for instance,powders, particles, capsules filled with these or their granulationproduct or mixture, tablets obtained by compression molding of these,and capsules filled with liquids, suspension, emulsion, etc., and thelike.

FIG. 2 is a diagram showing changes over time in the number of insolubleparticulate matter determined in Comparative Example 4, ComparativeExample 5, and Example 5.

FIG. 3 is a diagram showing changes in the plasma concentration ofunaltered form found in Comparative Example 6 and Example 6.

FIG. 4 is a diagram showing changes over time in the number of insolubleparticulate matter determined in Comparative Example 7, ComparativeExample 8, and Example 11.

FIG. 5 is a diagram showing changes over time in the number of insolubleparticulate matter determined in Comparative Example 9, ComparativeExample 10, and Example 12.

FIG. 6 is a diagram showing changes over time in the number of insolubleparticulate matter determined in Comparative Example 11, ComparativeExample 12, and Example 13.

FIG. 7 is a diagram showing changes over time in the number of insolubleparticulate matter determined in Comparative Example 13, ComparativeExample 14, and Example 14.

PREFERRED EMBODIMENTS OF THE INVENTION

The present invention will now be described with examples, but it is notlimited to these examples.

Whether or not a drug is difficult to absorb from the digestive tractdue to interaction with the digestive tract mucous components can beconfirmed by, for instance, the following method:

EXPERIMENT 1 COMPARATIVE EXAMPLE 1 Interaction Between Drug andDigestive Tract Mucous Layer Components

<Experimental Method> Tetracycline (TC hereafter) was dissolved in PBSbuffer to a drug concentration of 0.5 mg/ml. Moreover, a PBS buffercontaining 0.8% (w/v) pork stomach mucin, 6.2% (w/v) bovine serumalbumin, 4.92% (w/v) linoleic acid, 0.72% (w/v) cholesterol, 0.36% (w/v)phosphatidyl choline, 1.5% (w/v) Tween 80, and 0.04% (w/v) sodium azidewas prepared in accordance with the method of Angeta et al. (Angeta W.L. et al., Pharm. Res., 15, 66-71, 1998), and this liquid was used asthe artificial mucous liquid. An equilibrium dialysis cell consisting oftwo phases was used in the experiments. A dialysis membrane with afraction molecular weight of 50,000 (Spectra/Por®, SPECTRUM Lab., Inc.)was inserted between the 2 phases. One of the two phases served as theDonor phase (D phase hereafter) and one served as the Reservoir phase (Rphase hereafter). Two milliliters TC solution were introduced to the Dphase and 2 ml artificial mucous liquid were introduced to the R phaseand incubation was performed in a thermostatic cell (37° C., 150strokes/minute). The TC solution of the D phase was sampled and the drugconcentration was determined every hour for up to 5 hours. The drug wasdetermined by UV quantitative determination in accordance with themethod of Braybrooks (M. P. Braybrooks, J. Pharm. Pharmacol., 27, pp.508-515, 1975).

<Evaluation Method> The initial drug concentration of the D phase isC_(o) and the drug concentration at equilibrium (t=∞) is C_(∞). Formula(I) shows a as the ratio of drug present in the R phase at t=∞ that hasnot bound with artificial mucous component.a=C _(∞) /C _(o) −C _(∞)  (I)

When all of the drug that has moved to the R phase has been adsorbed onthe artificial mucous components, a=0, and when none has adsorbed, a=1.Therefore, a was used as a parameter that indicates adsorptivity ofdrugs on artificial mucous components.

-   -   C_(∞): calculated by deriving the drug concentration-time        formula and substituting t=∞.    -   C_(o): drug concentration when experiment started (0.5 mg/ml)    -   [Reference 1]

An experiment was performed and a was calculated by the same method asentered under Experiment 1 using artificial mucous obtained by mixing0.5 mg/ml TC solution to the D phase of the equilibrium dialysis celland 3% Eudragit™ EPO (Röhm GmRH) to the R phase.

EXAMPLE 1

1,650 g Eudragit™ E100 (Röhm GmRH) and Tween 80 at a ratio of 10:1 weredissolved in 12,000 g 1 mol/l aqueous hydrochloric acid.ethanol mixture(5:12) to obtain the spraying liquid. The spraying liquid was spraydried at a spraying speed of 30 g/minute, intake temperature of 85° C.,and exhaust temperature of 62-66° C. using the model L-8 Spray Dryer(Ohkawara Seisakujo). After drying for 24 hours at 40° C., a whitepowder was obtained (E-SD hereafter; used in the following Examples,Experiments, Comparative Examples, etc., unless otherwise specified). Anexperiment was performed and a was calculated by the same method as inExperiment 1 using artificial mucous obtained by dissolving 0.5 mg/ml TCsolution in the D phase of the equilibrium dialysis cell and 3% E-SD inthe R phase.

[Control 1]

An experiment was performed and a was calculated by the same method asin Experiment 1 using 0.5 mg/ml TC solution in the D phase of theequilibrium dialysis cell and PBS buffer in the R phase.

Evaluation

With the a value obtained in Control 1 serving as 100, the a value ofComparative Example 1 (Experiment 1) and Example 1 to this value (%) isshown in Table 1. TABLE 1 Comparative Control 1 Example 1 Reference 1Example 1 a (% of Control) 100 48.8 74.3 71.9

Results and Discussion

The a value of Comparative Example 1 (Experiment 1) was approximately50% that of Control 1, indicating that the TC was firmly bound to theartificial mucous components. In contrast to this, according to theresults of Example 1, the a value was improved to approximately 70% thatof Control 1 by mixing aminoalkyl methacrylate copolymer E and acidicsubstance in the artificial mucous. Consequently, this indicates that acomposition in which aminoalkyl methacrylate copolymer E and an acidicsubstance, for instance, hydrochloric acid, etc., have been uniformlymixed has the effect of increasing the ratio of drug that is not boundto mucus by co-existing with mucous components. Furthermore, the resultsof Reference Example 1 revealed that in vitro there was an improvementin the a value to at least approximately 70% that of Control 1, but thisresult could not be confirmed in vivo.

EXPERIMENT 2 Control 2

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Eighty mg TC were weighed out and dissolvedin 100 ml PBS buffer to obtain an aqueous 0.8 mg/ml TC solution(hereafter referred to as solution A). Ten milliliters solution A and 10ml PBS buffer were mixed with a vortex mixer and mixture in an amountcorresponding to 10 mg/kg TC was administered through the intestinalloop. Blood was drawn from the jugular vein 0, 0.25, 0.5 and 1 hourafter administration and the plasma concentration of unaltered form(μg/ml) was determined by high-performance liquid chromatography inaccordance with the Nilsson-Ehle method (I. Nilsson-Ehle, Acta Path.microbiol. scand. Sect. B, Suppl. 259: pp. 61-66 (1977)). The maximumplasma concentration (Cmax) and area under concentration curve (AUC)were calculated from the changes in the plasma concentration that wereobtained.

EXAMPLE 2

Six grams E-SD were weighed out and dissolved in 100 ml PBS buffersolution to obtain an aqueous 60 mg/ml solution (solution B hereafter).Ten milliliters solution A and 10 ml solution B were mixed with a vortexmixer. The solution was administered through the rat intestinal loop andthe plasma concentration of unaltered form was determined by the samemethod as in Experiment 2. The Cmax and AUC were calculated from thechanges in the plasma concentration that were obtained.

EXAMPLE 3

Eudragit™ EPO (Röhm GmRH) was dissolved in aqueous hydrochloric acid andlyophilized (the lyophilized product is E-FD hereafter). Six g E-FD wereweighed out and dissolved in 100 ml PBS buffer solution to obtain anaqueous 60 mg/ml solution (solution C hereafter). Ten milliliterssolution A and 10 ml solution C were mixed with a vortex mixer. Thesolution was administered through the rat intestinal loop and the plasmaconcentration of unaltered form was determined by the same method as inExperiment 2. The Cmax and AUC were calculated from the changes in theplasma concentration that were obtained.

COMPARATIVE EXAMPLE 2

(Confirmation of Improvement of Absorption by Enteric Polymer Base)

Eudragit™ L100 (Röhm GmRH) was dissolved in aqueous sodium hydroxidesolution and lyophilized (the lyophilized product is L-FD hereafter).Six g L-FD were weighed out and dissolved in 100 ml PBS buffer solutionto obtain an aqueous 60 mg/ml solution (solution D hereafter). Tenmilliliters solution A and 10 ml solution D were mixed with a vortexmixer. The solution was administered through the rat intestinal loop andthe plasma concentration of unaltered form was determined by the samemethod as in Experiment 2. The Cmax and AUC were calculated from thechanges in the plasma concentration that were obtained. The Cmax and AUCthat were found in Experiment 2, Comparative Example 2, Example 2 andExample 3 are shown in Table 2. TABLE 2 Cmax (μg/ml) AUC (μg · min/ml)Control 2 0.79 ± 0.31  22.05 ± 2.84 Example 2 3.47 ± 0.01 158.80 ± 1.80Example 3 3.64 ± 0.32 174.53 ± 13.78 Comparative 0.63 ± 0.07  16.79 ±3.26 Example 2

-   -   (Mean value±S.D.)

Results and Discussion

There was a marked increase in Cmax and AUC in Example 2 and Example 3when compared to Experiment 2. In Example 2, the Cmax was approximately4-times that of Experiment 2 and the AUC was approximately 7-times thatof Experiment 2. In Example 3, Cmax was approximately 4.5-times that ofExperiment 2 and AUC was approximately 8-times that of Example 2. Basedon these results, it is clear that the plasma concentration of TC isincreased by using aminoalkyl methacrylate copolymer E and acidicsubstance. On the other hand, Cmax and AUC of Comparative Example 2 inwhich Eudragit™ L100, which is an enteric polymer, was used were notdifferent from those of Experiment 2. Consequently, it became clear thata composition in which aminoalkyl methacrylate copolymer E and acidicsubstance, such as hydrochloric acid, etc., have been uniformly mixedhas the effect of promoting absorption of TC from the digestive tract invivo.

COMPARATIVE EXAMPLE 3

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. 80 mg TC were weighed out and dissolved in100 ml PBS buffer to obtain an aqueous 0.8 mg/ml TC solution (solution Ahereafter). Six grams Eudragit™ EPO (Röhm GmRH) were weighed out anddispersed in 100 ml PBS buffer to obtain a 60 mg/ml dispersion (solutionE hereafter). Ten milliliters solution A and 10 ml solution E were mixedwith a vortex mixer. This mixture was circulated through the ratintestinal loop and the plasma concentration of unaltered form wasdetermined by the same method as in Experiment 2. The maximum plasmaconcentration (Cmax) and area under concentration curve (AUC) werecalculated from the changes in the plasma concentration that wereobtained. The Cmax and AUC found in Experiment 2, Example 3 andComparative Example 3 are shown in Table 3. TABLE 3 Cmax (μg/ml) AUC (μg· min/ml) Control 2 0.79 ± 0.31  22.05 ± 2.84 Example 3 3.47 ± 0.01158.80 ± 1.80 Comparative 0.64 ± 0.24  11.80 ± 4.88 Example 3(Mean value ± S.D., n = 3)

Results and Discussion

As with E-SD, Eudragit™ EPO prevented binding of TC with artificialmucus in experiments using in vitro equilibrium dialysis, but the effectof promoting absorption of TC was not seen in vivo. The reason for thisis apparently that although EPO was dissolved in the linoleic acidcontained in the artificial mucus so that interaction was inhibited invitro, in vivo there was not sufficient acidic oil, such as linoleicacid, etc., to dissolve the EPO that had been administered andtherefore, absorption of the TC was not improved. Consequently, itappears that absorption of a drug can be improved using Eudragit™ E byuniformly mixing the Eudragit™ E and acidic substance. Moreover, when adrug and Eudragit™ E are orally administered, there is a chance thatdigestive tract absorption of the drug will not be improved in humanswith achlorhydria because the Eudragit™ E will not be dissolved in thesmall intestine of course, or in the stomach. Consequently, it appearsthat by unifommly mixing Eudragit™ E and acidic substance, it ispossible to improve with more certainty drug absorption using Eudragit™E.

EXPERIMENT 3 Control 3

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Twenty milligrams TC and 500 mg lactose wereweighed out and thoroughly mixed with a mortar and pestle. Fifty-twomilligrams of the mixed powder that was obtained were molded into tabletform and administered through the rat intestinal loop using a plastictube. Blood was drawn from the jugular vein 0, 0.25, 0.5 and 1 hourafter administration and the plasma concentration of unaltered form(μg/ml) was determined by high-performance liquid chromatography by thesame method as in Experiment 2. Cmax and AUC were calculated from thechanges in the plasma concentration that were obtained.

EXAMPLE 4

Twenty milligrams TC and 500 mg E-SD were weighed out and thoroughlymixed with a mortar and pestle. Fifty-two milligrams of the mixed powderthat was obtained was molded into tablet form. The tablet was circulatedthrough the rat intestinal loop and the plasma concentration ofunaltered form was determined by the same method as in Experiment 3.Cmax and AUC were calculated from the changes in the plasmaconcentration that were obtained. Cmax and AUC that were found inExperiment 3 and Example 4 are shown in Table 4. TABLE 4 Cmax (μg/ml)AUC (μg · min/ml) Test 3 0.36 ± 0.06  5.37 ± 0.88 Example 4 1.05 ± 0.3830.41 ± 2.85(Mean value ± S.D.)

Results and Discussion

An increase in the plasma concentration of the drug was seen in Example4 when compared to Experiment 3. Cmax was approximately 3-times that ofExperiment 3 and AUC was approximately 6-times that of Experiment 3 inExample 4. Consequently, it became clear that aminoalkyl methacrylatecopolymer E has the effect of promoting absorption of a drug by beingdissolved in the digestive tract, whether it is administered in solutionform or solid form.

Compound B in Experiment 4, Experiment 5, and Example 5, etc., below is[1-hydroxy-2-imidazo-(1,2-a)pyridin-3-ylethylidene]bis-phosphonate),which was made by the method in Japanese Kokoku Patent No. Hei 6-99457.

EXPERIMENT 4 COMPARATIVE EXAMPLE 4

Five milliliters of an aqueous 0.5 mg/ml compound B solution wereprepared and 5 ml distilled water were added to this and thoroughlymixed to obtain the prepared liquid. Another 2 ml distilled water wereadded to this liquid to obtain control liquid A. The number of insolubleparticulate matter (10 μm or larger) in control liquid A was determined0, 15, 30 and 60 minutes after preparation using an insolubleparticulate matter gauge (brand name HIAC/ROYCO®, Pacific Scientific).

EXPERIMENT 5 COMPARATIVE EXAMPLE 5

Five milliliters of an aqueous 0.5 mg/ml compound B solution wereprepared and 5 ml distilled water were added to this and thoroughlymixed to obtain the prepared liquid. Two milliliters of aqueous 10 mg/mlcalcium chloride.2H₂O solution were added to this liquid to obtaincontrol liquid B. The number of insoluble particulate matter (10 μm orlarger) in control liquid B was determined 0, 15, 30 and 60 minutesafter preparation by the same method as in Experiment 4.

EXAMPLE 5

Five milliliters each of aqueous 0.05% E-SD solution, aqueous 0.1% E-SDsolution, aqueous 1.0% E-SD solution, and aqueous 2.0% E-SD solutionwere added to 5 ml of aqueous 0.5 mg/ml compound B solution andthoroughly mixed to obtain aqueous compound B solutions comprising0.025%, 0.05%, 0.5% and 1.0% E-SD. Two milliliters aqueous 10 mg/mlcalcium chloride solution were added to each of these prepared solutionsand the number of insoluble particulate matter (10 μm or larger) wasdetermined 0, 15, 30 and 60 minutes after addition by the same method asin Experiment 4.

Results and Discussion

FIG. 2 shows changes over time in the number of insoluble particulatematter determined in Comparative Example 4, Comparative Example 5, andExample 5. Based on the results in Comparative Examples 4 and 5, anincrease in the number of insoluble particulate matter was seen whenaqueous calcium chloride solution was added to the aqueous compound Bsolution. In contrast to this, the formation of insoluble particulatematter was inhibited dependent on the E-SD concentration in Example 5when the E-SD was dissolved, that is, when aqueous calcium chloridesolution was added to the aqueous compound B solution comprisingaminoalkyl methacrylate copolymer E and hydrochloric acid. Results wereseen from a low concentration of at least 0.05%. Consequently, it isconfirmed that aminoalkyl methacrylate copolymer E in the presence ofacidic substance has the effect of inhibiting the formation of aninsoluble complex between drug and metal ions.

EXPERIMENT 6 COMPARATIVE EXAMPLE 6

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Eighty milligrams compound B were weighedout and dissolved in 100 ml PBS buffer to obtain an aqueous 0.8 mg/ml TCsolution (solution A hereafter). Ten milliliters solution A and 10 mlPBS were mixed with a vortex mixer. This mixed solution was administeredthrough the rat intestinal loop in an amount corresponding to 10 mg/kgcompound B. Blood was drawn from the jugular vein 0, 0.25, 0.5 and 1hour after administration and the plasma concentration of unaltered form(ng/ml) was determined by the fluorescence detection method usinghigh-performance liquid chromatography in accordance with the method ofUsui et al. (T. Usui et al., J. Chromatogr. B 652 (1994)).

EXAMPLE 6

Four grams E-SD were weighed out and dissolved in 100 ml PBS buffersolution to obtain an aqueous 40 mg/ml solution (solution B hereafter).Ten milliliters solution A and 10 ml solution B were mixed with a vortexmixer. The mixed was administered through the rat intestinal loopsolution in an amount corresponding to 10 mg/kg compound B and theplasma concentration of unaltered form was determined by the same methodas in Comparative Example 6.

Results and Discussion

FIG. 3 shows the changes in the plasma concentration of unaltered formfound in Comparative Example 6 and Example 6. These results indicatethat aminoalkyl methacrylate copolymer E improves oral absorption ofcompound B, which forms a slightly soluble complex with the calcium ionsthat are present in the digestive tract mucous membrane and/or mucouslayer.

EXPERIMENT 7 Control 4

Ten milligrams compound B and 190 mg lactose were mixed and tablets wereprepared by tableting under a tableting pressure of 40 kg/cm² using anoil press. The tablets for the control were orally administered togetherwith 30 ml water to beagles (15-24 months old) under fasting conditions.Approximately 3 ml blood were drawn from the brachial veins of the frontlimbs over time up to 8 h after administration and the plasmaconcentration of unaltered form (ng/ml) was determined by the samemethod as in Comparative Example 6. The maximum plasma concentration(Cmax) and area under concentration curve (AUC) were calculated from thechanges in the plasma concentration that were obtained.

EXAMPLE 7

Ten milligrams compound B, 125 mg E-SD, and 65 mg lactose were mixed andtablets were prepared by tableting under a tableting pressure of 40kg/cm² using an oil press. These tablets were orally administered tobeagles, blood was drawn and the plasma concentration of unaltered formwas determined under the same conditions as in Experiment 7. Cmax andAUC were determined from changes in the plasma concentration that wereobtained. Cmax and AUC that were found in Control 4 and Example 7 areshown in Table 5. TABLE 5 Cmax (ng/ml) AUC 0.8 h (ng · h/ml) Control 4 7.7 ± 3.9  18.9 ± 7.1 Example 7 56.6 ± 26.0 108.1 ± 64.0(Mean value ± S.D., n = 6)

Results and Discussion

Cmax and AUC of Example 7 were approximately 7.4-times and approximately5.7-times those of Control 4, respectively, with there being a markedincrease in Cmax and AUC when compared to Control 4.

It became clear from this finding that aminoalkyl methacrylate copolymerE has the effect of promoting absorption of compound B from thedigestive tract.

EXAMPLE 8 Enteric Tablets

Tablets coated with 1.2% HPMC were obtained by spraying (sprayingconditions: number of revolutions 12 rpm, intake temperature 56-60° C.,exhaust temperature 44-46° C., spraying speed 4-10 g/min) the tabletsobtained in Example 7 with an aqueous 10% HPMC (brand name TC-5E,Shin-etsu Chemical Co., Ltd.) solution using Hicoater (brand name HCT-30Hicoater, Freund). Enteric coated tablets were prepared by coating with2.7% enteric coating base by spraying (spraying conditions: number ofrevolutions 12 rpm, intake temperature 52° C., exhaust temperature 40°C., spraying speed 4-8 g/min) a solution of 10% (enteric base (EudragitL: Triethyl citrate=9:1) in a water/ethanol (1:17) mixture using aHicoater. These tablets were orally administered to beagles, blood wasdrawn, and the plasma concentration of unaltered form was determinedunder the same conditions as in Experiment 7. Cmax and AUC werecalculated from the changes in the plasma concentration that wereobtained.

EXAMPLE 9 Sustained-Release Tablets

Tablets were prepared by mixing 10 mg compound B, 125 mg E-SD, 20 mgpolyethylene oxide (brand name Polyox WSR303, Union Carbide), and 45 mgMacrogol 6000 and tableting under a tableting pressure of 40 kg/cm²using an oil press. These tablets were orally administered to beagles,blood was drawn, and the plasma concentration of unaltered form wasdetermined under the same conditions as in Experiment 7. Cmax and AUCwere calculated from the changes in the plasma concentration that wereobtained.

EXAMPLE 10 Timed-Release Tablets

Tablets were prepared to obtain core tablets by mixing 10 mg compound B,125 mg E-SD, and 65 mg sucrose and tableting under a tableting pressureof 40 kg/cm² using an oil press. Fifty milligrams polyethylene oxide(brand name Polyoxy WSR303) and 250 mg Macrogol 6000 were mixed toprepare polyethylene oxide/Macrogol 6000. Half was added to a tabletingmortar and then the core was placed in the center of the mortar. Next,half of the remainder of the above-mentioned mixed powder was added tothe mortar and tablets with an outer layer were prepared by tabletingunder a tableting pressure of 40 kg/cm² using an oil press. Thesedry-coated tablets were orally administered to beagles, blood was drawnand the plasma concentration of unaltered form was determined under thesame conditions as in Experiment 7. Cmax and AUC were calculated fromthe changes in the plasma concentration that were obtained. Cmax and AUCthat were found in Control 4, Example 8, Example 9, and Example 10 areshown in Table 6. TABLE 6 Cmax (ng/ml) AUC 0.8 h (ng · h/ml) Control 4 7.7 ± 3.9  18.9 ± 7.1 Example 8 14.0 ± 13.0  39.7 ± 25.4 Example 9 35.3± 25.3 102.2 ± 88.2 Example 10 20.0 ± 9.6  63.9 ± 32.9(Mean value ± S.D., n = 3-6)

Results and Discussion

Example 8, Example 9, and Example 10 showed a marked increase in theCmax and AUC when compared to Control 4. It became clear from theseresults that absorption of compound B from the digestive tract ispromoted with pharmaceutical preparations in which aminoalkylmethacrylate copolymer E and acidic substance have been uniformly mixedin a variety of preparation types, including enteric pharmaceuticalpreparations, sustained-release pharmaceutical preparations,timed-release pharmaceutical preparations, etc.

Compound C below is incadronate[(cycloheptylamino)-methylene]bis-phosphonate made by the method inJapanese Patent No. Hei 7-629.

EXPERIMENT 8 COMPARATIVE EXAMPLE 7

Five milliliters of aqueous 0.5 mg/ml compound C solution were prepared.Five milliliters distilled water and 2 ml of an aqueous 15.12 mg/mlsodium bicarbonate solution were added to this and thoroughly mixed toobtain a prepared liquid. Another 2 ml distilled water were added tothis liquid. The number of insoluble particulate matter (10 μm orlarger) was determined 0, 15, 30 and 60 minutes after addition using aninsoluble particulate matter gauge (brand name HIAC/ROYCO®, PacificScientific).

COMPARATIVE EXAMPLE 8

Five milliliters of an aqueous 0.5 mg/ml compound C solution wereprepared. Five milliliters distilled water and 2 ml of an aqueous 15.12mg/ml sodium bicarbonate solution were added to this and thoroughlymixed to obtain a prepared liquid. Two milliliters of an aqueous 10mg/ml calcium chloride.2H₂O solution were added to this liquid and thenumber of insoluble particulate matter (10 μm or larger) were determined0, 15, 30, and 60 minutes after addition by the same method as inExperiment 8.

EXAMPLE 11

Five milliliters of an aqueous 0.5 mg/ml compound C solution wereprepared. Five milliliters of an aqueous 30 mg/ml E-SD solution and 2 mlof an aqueous 15.12 mg/ml sodium bicarbonate solution were added to thisand thoroughly mixed to obtain a prepared solution. Then 2 ml of anaqueous 10 mg/ml calcium chloride.2H₂O solution were added to thisliquid. The number of insoluble particulate matter (10 μm or larger) wasdetermined 0, 15, 30 and 60 minutes after addition by the same method asin Example 8. Changes over time in the number of insoluble particulatematter determined in above-mentioned Comparative Example 7, ComparativeExample 8, and Example 11 are shown in FIG. 4.

Results and Discussion

According to the results of Comparative Example 7 and ComparativeExample 8, an increase in the number of insoluble particulate matter wasseen when aqueous calcium chloride solution was added to aqueouscompound C solution. The formation of insoluble particulate matter wasinhibited when aqueous calcium chloride solution was added to aqueouscompound C solution in which E-SD had been dissolved in Example 11. Thisconfirms that aminoalkyl methacrylate copolymer E has the effect ofinhibiting the formation of a slightly soluble complex between compoundC and metal (calcium) ions.

Compound D (etidronate) below is(1-hydroxyethylidene)-1,1-bisphosphonate.

EXPERIMENT 9 COMPARATIVE EXAMPLE 9

Five milliliters of aqueous 0.5 mg/ml compound D solution were preparedand 5 ml distilled water and 0.1 ml aqueous 15.12 mg/ml sodiumbicarbonate solution were added to this and thoroughly mixed to obtainthe prepared liquid. Another 2 ml distilled water were added to thisliquid, and the number of insoluble particulate matter (2 μm or larger)was determined 0, 15, 30 and 60 minutes after addition using aninsoluble particulate matter gauge (brand name HIAC/ROYCO®, PacificScientific).

COMPARATIVE EXAMPLE 10

Five milliliters aqueous 0.5 mg/ml compound D solution were prepared and5 ml distilled water and 0.1 ml aqueous 15.12 mg/ml sodium bicarbonatesolution were added to this, and thoroughly mixed to obtain the preparedliquid. Two milliliters aqueous 10 mg/ml calcium chloride.2H₂O solutionwere added to this, and the number of insoluble particulate matter (2 μmor larger) was determined 0, 15, 30 and 60 minutes after addition by thesame method as in Experiment 9.

EXAMPLE 12

Five milliliters aqueous 0.5 mg/ml compound D solution were prepared andthen 5 ml aqueous 30 mg/ml E-SD solution and 0.1 ml aqueous 15.12 mg/mlsodium bicarbonate solution were added to this and thoroughly mixed toobtain the prepared liquid. Two milliliters aqueous 10 mg/ml calciumchloride.2H₂O solution were added to this and the number of insolubleparticulate matter (2 μm or larger) was determined 0, 15, 30, and 60minutes after addition by the same method as in Experiment 9. Changesover time in the number of insoluble particulate matter determined inabove-mentioned Comparative Example 9, Comparative Example 10, andExample 12 are shown in FIG. 5.

Results and Discussion

According to the results in Comparative Example 9 and ComparativeExample 10, there was an increase in the number of insoluble particulatematter when aqueous calcium chloride solution was added to aqueouscompound D solution. Formation of insoluble particulate matter wasinhibited when aqueous calcium chloride solution was added to aqueouscompound D solution in which E-SD had been dissolved in Example 12. Thisconfirms that aminoalkyl methacrylate copolymer E has the effect ofinhibiting the formation of a slightly soluble complex between compoundD and metal (calcium) ions.

Compound E (alendronate) below is 4-amino-1-hydroxy butylidene1,1-bisphosphonate.

EXPERIMENT 10 COMPARATIVE EXAMPLE 11

Five milliliters of an aqueous 0.5 mg/ml compound E solution wereprepared and 5 ml distilled water and 3 ml aqueous 15.12 mg/ml sodiumbicarbonate solution were added to this and thoroughly mixed to obtain aprepared liquid. Another 2 ml distilled water were added to this liquid,and the number of insoluble particulate matter (2 μm or larger) wasdetermined 0, 15, 30, and 60 minutes after addition using an insolubleparticulate matter gauge (brand name HIAC/ROYCO®, Pacific Scientific).

COMPARATIVE EXAMPLE 12

Five milliliters aqueous 0.5 mg/ml compound E solution were prepared and5 ml distilled water and 3 ml aqueous 15.12 mg/ml sodium bicarbonatesolution were added to this and thoroughly mixed to obtain the preparedliquid. Two milliliters aqueous 10 mg/ml calcium chloride.2H₂O solutionwere added to this liquid, and the number of insoluble particulatematter (2 μm or larger) was determined 0, 15, 30 and 60 minutes afteraddition by the same method as in Experiment 10.

EXAMPLE 13

Five milliliters aqueous 0.5 mg/ml compound E solution were prepared and5 ml aqueous 30 mg/ml aqueous E-SD solution and 3 ml aqueous 15.12 mg/mlsodium bicarbonate solution were added to this and thoroughly mixed toobtain the prepared liquid. Two milliliters aqueous 10 mg/ml calciumchloride.2H₂O solution were added to this liquid, and the number ofinsoluble particulate matter (2 μm or larger) was determined 0, 15, 30,and 60 minutes after addition as in Experiment 10. The changes over timein the number of insoluble particulate matter determined inabove-mentioned Comparative Example 11, Comparative Example 12, andExample 13 are shown in FIG. 6.

Results and Discussion

According to the results in Comparative Example 11 and ComparativeExample 12, there was an increase in the number of insoluble particulatematter when aqueous calcium chloride solution was added to aqueouscompound E solution. The formation of insoluble particulate matter wasinhibited when aqueous calcium chloride solution was added to aqueouscompound E solution in which E-SD had been dissolved in Example 13. Thisconfirms that aminoalkyl methacrylate copolymer E has the effect ofinhibiting the formation of a slightly soluble complex between compoundE and metal (calcium) ions.

EXPERIMENT 11 COMPARATIVE EXAMPLE 13 Experiment Using Another Metal Ion,Magnesium

Five milliliters aqueous 0.5 mg/ml compound B solution were prepared and5 ml distilled water and 0.1 ml aqueous 15.12 mg/ml sodium bicarbonatesolution were added and thoroughly mixed to obtain the prepared liquid.Another 2 ml distilled water were added to this solution and the numberof insoluble particulate matter (2 μm or larger) was determined 0, 15,30, and 60 minutes after addition using an insoluble particulate mattergauge (HIAC/ROYCO®, Pacific Scientific).

COMPARATIVE EXAMPLE 14

Five milliliters aqueous 0.5 mg/ml compound B solution were prepared and5 ml distilled water and 0.1 ml aqueous 15.12 mg/ml sodium bicarbonatesolution were added to this and thoroughly mixed to obtain the preparedliquid. Two milliliters aqueous 10 mg/ml magnesium chloride.6H₂Osolution were added to this prepared liquid, and the number of insolubleparticulate matter (2 μm or larger) was determined 0, 15, 30 and 60minutes after addition by the same method as in Experiment 11.

EXAMPLE 14

Five milliliters aqueous 0.5 mg/ml compound B solution were prepared and5 ml aqueous 30 mg/ml E-SD solution and 0.1 ml aqueous 15.12 mg/mlsodium bicarbonate solution were added to this and thoroughly mixed toobtain a prepared liquid. Two milliliters aqueous 10 mg/ml magnesiumchloride.6H₂O were added to this prepared liquid, and the number ofinsoluble particulate matter (2 μm or larger) was determined 0, 15, 30and 60 minutes after addition by the same method as in Experiment 11.The changes over time in the number of insoluble particulate matterdetermined in above-mentioned Comparative Example 13, ComparativeExample 14, and Example 14 are shown in FIG. 7.

Results and Discussion

According to the results in Comparative Example 13 and ComparativeExample 14, there was an increase in the number of insoluble particulatematter when aqueous magnesium chloride solution was added to aqueouscompound B solution. The formation of insoluble particulate matter wasinhibited when aqueous magnesium chloride solution was added to aqueouscompound B solution in which E-SD had been dissolved in Example 14. Thisconfirms that aminoalkyl methacrylate copolymer E has the effect ofinhibiting the formation of slightly soluble complex between compound Band metal (magnesium) ions.

EXAMPLE 15 Amount of Acid and Type of Acid Added to Eudragit E

First, 1,500 g Eudragit™ E100 and 150 g Tween 80 were dissolved in amixture of 9,000 g ethanol and 3,000 g 1 mol/l hydrochloric acid to makethe spraying liquid. The spraying liquid was spray dried underconditions of a spraying speed of 30 g/min, an intake temperature of 85°C., and an exhaust temperature of 62-66° C. using the model L-8 spraydryer (Ohkawara Seisakujo) and dried for 24 hours at 40° C. to obtain awhite powder. When 1 g of this product was added to 15 ml purifiedwater, it completely dissolved. Moreover, this product was stable withno aggregation during storage.

EXAMPLE 16

First, 2.9 g Eudragit™ EPO, which is a micropowder of Eudragit™ E, wereadded to 50 g purified water to make the test liquid. When 650 mg citricacid were added to this test liquid, the Eudragit™ E in the test liquidcompletely dissolved. A white lyophilized product was obtained when asolution of 0.25 g Tween 80 dissolved in this liquid was lyophilizedusing the model FD-81 lyophilization device (Tokyo Rika Kikai Co.,Ltd.). When 1 g of this product was added to 15 g purified water, itcompletely dissolved.

EXAMPLE 17

First, 2.9 g Eudragit™ EPO were added to 50 g purified water to make thetest liquid. When 650 mg tartaric acid were added to this test liquid,the Eudragit™ E in the test liquid completely dissolved. A whitelyophilized product was obtained when a solution of 0.29 g Tween 80dissolved in this liquid was lyophilized as in Example 16. When 1 g ofthis product was added to 15 g purified water, it completely dissolved.

EXAMPLE 18

3.3 g Eudragit™ EPO were added to 50 g purified water to make the testliquid. When 650 mg D,L-malic acid were added to this test liquid, theEudragit™ E in the test liquid completely dissolved. A white lyophilizedproduct was obtained when a solution of 0.33 g Tween 80 dissolved inthis liquid was lyophilized as in Example 16. When 1 g of this productwas added to 15 g purified water, it completely dissolved.

Results and Discussion

The results of Example 15 indicates that it is possible to prepareaminoalkyl methacrylate copolymer E to which an acid that can dissolvein purified water has been added by adding 0.075 parts by weight ofhydrochloric acid to 1 part by weight of Eudragit™ E. Consequently, thiscomposition apparently will dissolve in the stomach as well as in theentire digestive tract where water can be present to improve drugabsorption in the digestive tract. The results of Examples 16˜18 showthat it is possible to prepare aminoalkyl methacrylate copolymer E thatwill dissolve in purified water, regardless of the type of acid, such ascitric acid, tartaric acid, malic acid, etc.

EXPERIMENT 12 (Control 5)<Type of Acid: Confirmation of Performance InVivo>

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. A PBS solution of 0.4 mg/ml compound B wasadministered through this loop so that the dose would be 10 mg/kgcompound B. Blood was drawn from the jugular vein 0, 0.25, 0.5 and 1hour after administration and the plasma concentration of unaltered form(ng/ml) was determined by the same method as in Control 4. The areaunder concentration curve (AUC) was calculated from the changes in theplasma concentration that were obtained.

EXAMPLE 19

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Administration liquid of the spray-driedproduct in Example 15 dissolved in a PBS solution of 0.4 mg/ml compoundB to a concentration of 0.5 mg/ml was administered so that the dosewould be 10 mg/kg compound B. Blood was drawn from the jugular vein 0,0.25, 0.5 and 1 hour after administration and the plasma concentrationof unaltered form (ng/ml) was determined by the same method as inControl 4. The area under concentration curve (AUC) was calculated fromthe changes in the plasma concentration that were obtained.

EXAMPLE 20

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Administration liquid of the lyophilizedproduct in Example 16 dissolved in a PBS solution of 0.4 mg/ml compoundB to a concentration of 0.5 mg/ml was administered so that the dosewould be 10 mg/kg compound B. Blood was drawn from the jugular vein 0,0.25, 0.5 and 1 hour after administration and the plasma concentrationof unaltered form (ng/ml) was determined by the same method as inControl 4. The area under concentration curve (AUC) was calculated fromthe changes in the plasma concentration that were obtained.

EXAMPLE 21

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Administration liquid of the lyophilizedproduct in Example 17 dissolved in a PBS solution of 0.4 mg/ml compoundB to a concentration of 0.5 mg/ml was administered so that the dosewould be 10 mg/kg compound B. Blood was drawn from the jugular vein 0,0.25, 0.5 and 1 hour after administration and the plasma concentrationof unaltered form (ng/ml) was determined by the same method as inControl 4. The area under concentration curve (AUC) was calculated fromthe changes in the plasma concentration that were obtained.

EXAMPLE 22

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Administration liquid of the lyophilizedproduct in Example 18 dissolved in a PBS solution of 0.4 mg/ml compoundB to a concentration of 0.5 mg/ml was administered so that the dosewould be 10 mg/kg compound B. Blood was drawn from the jugular vein 0,0.25, 0.5 and 1 hour after administration and the plasma concentrationof unaltered form (ng/ml) was determined by the same method as inControl 4. The area under concentration curve (AUC) was calculated fromthe changes in the plasma concentration that were obtained.

EXAMPLE 23

Laparotomy was performed under pentobarbital (brand name Nembutal,Dainabot Co., Ltd.) anesthetization in Wistar male rats (8 weeks old)and the Treitz's ligament and ileocecal juncture were bound with threadto form an intestinal loop. Next, 111 mg of a solution prepared bydissolving 400 mg Eudragit™ EPO and 40 mg Tween 80 in 4 g linoleic acidwere measured out and added to 20 mL of a PBS solution of 0.4 mg/mlcompound B to prepare the administration liquid. This administrationliquid was administered through the loop so that the dose would be 10mg/kg compound B. Blood was drawn from the jugular vein 0, 0.25, 0.5 and1 hour after administration and the plasma concentration of unalteredform (ng/ml) was determined by the same method as in Control 4. The areaunder concentration curve (AUC) was calculated from the changes in theplasma concentration that were obtained. The AUC found in Control 5 andExamples 19˜23 are shown in Table 7. TABLE 7 AUC (ng · h/ml) Control 5 42.2 ± 11.3 Example 19  393.6 ± 135.7 Example 20 1367.8 ± 1054.5Example 21  339.1 ± 162.0 Example 22  635.6 ± 381.2 Example 23  504.0 ±698.0(Mean value ± S.D., n = 3)

Results and Discussion

The AUC in any of Examples 19˜23 was high in comparison to Control 5.

The AUC was high in comparison to Control 5 whether hydrochloric acid,citric acid, tartaric acid, malic acid, linoleic acid, etc., was used asthe type of acidic substance uniformly mixed in Eudragit E.Consequently, it was clear that the acidic substance uniformly mixedwith aminoalkyl methacrylate copolymer E has the effect of promotingabsorption of compound B from the digestive tract, regardless of thetype of acid.

EXPERIMENT 13 Control 6

Ten milligrams compound B and 190 mg lactose were mixed and controltablets were prepared by tableting under a tableting pressure of 40kg/cm² using an oil press. Fifty grams of feed (Science Diet®, NipponHill's) were given to beagles (15-24 months old) that had been fastedover night and 30 minutes later, the control tablets were orallyadministered together with 30 ml water. Approximately 3 ml blood weredrawn from the brachial veins of the front limbs over time up to 14 hafter administration and the plasma concentration of unaltered form(ng/ml) was determined by the same method as Comparative Example 6. Themaximum plasma concentration (Cmax) and area under concentration curve(AUC) were calculated from the changes in the plasma concentration thatwere obtained.

EXAMPLE 24

Ten milligrams compound B, 125 mg E-SD, and 65 mg sucrose were mixed andtablets were prepared by tableting under a tableting pressure of 40kg/cm² using an oil press to obtain a core. Two-hundred milligramspolyethylene oxide (Polyox WSR303, Union Carbide Co., Ltd.) and 100 mgMacrogol 6000 were mixed to prepare polyethylene oxide/Macrogol 6000mixed powder. Half was added to a mortar for tableting and then the corewas placed in the center of the mortar. Next, half of the remainder ofthe above-mentioned mixed powder was added to the mortar and tabletswith an outer layer were prepared by tableting under a tabletingpressure of 40 kg/cm² using an oil press. This dry-coated tablet wasorally administered to beagles under the same conditions as inExperiment 13, blood was drawn over time up to 14 h afteradministration, and the plasma concentration of unaltered form wasdetermined. Cmax and AUC were calculated from the changes in the plasmaconcentration that were obtained. The results of Experiment 13 andExample 24 are shown in Table 8. TABLE 8 Cmax (ng/ml) AUC (ng · h/ml)Test 13  1.0 ± 1.0  4.7 ± 3.9 Example 24 12.3 ± 5.4 55.8 ± 26.4(Mean value ± S.D., n = 3-6)

Results and Discussion

Compound B is a drug that is readily affected by food and, as shown bythe results of Experiment 13, it has a low Cmax and AUC when taken withfood. In contrast to this, the Cmax and AUC of Example 24 increased toapproximately 12-times those of experiment 13. This results indicatethat a reduction in absorption of a drug due to the effects of food canbe prevented by using a timed-release pharmaceutical preparation withwhich aminoalkyl methacrylate copolymer E and an acidic substance, suchas hydrochloric acid, etc., has been uniformly mixed.

Possibility of Industrial Application

Aminoalkyl methacrylate copolymer E, which is used as the effectivecomponent in the present invention, has the effect of enhancing drugpermeability in the digestive tract mucous membrane and/or mucous layerand therefore is useful as an excellent agent for improving oralabsorption. The pharmaceutical composition of the present invention canenhance drug permeability by the effect of inhibiting a reduction indrug permeability of the mucous layer based on interaction between thecomponents of the digestive tract mucous membrane and/or mucous layerand drug and thereby realize excellent oral absorptivity of drugs whoseoral absorption has been considered to be reduced in the past. Moreover,in addition to drugs that are difficult to absorb, the pharmaceuticalcomposition of the present invention is ideal for drugs that show normalabsorptivity and therefore, it can be widely used.

1. A pharmaceutical composition for oral use with improved absorption,which comprises drug, aminoalkyl methacrylate copolymer E, and acidicsubstance and which is made by bringing said 3 components together anduniformly mixing at least the above-mentioned polymer andabove-mentioned acidic substance.
 2. The pharmaceutical composition ofclaim 1, wherein the drug, aminoalkyl methacrylate copolymer E, andacidic substance are uniformly mixed.
 3. The pharmaceutical compositionof claim 1 or 2, wherein the amount of aminoalkyl methacrylate copolymerE added is 0.01 part by weight or more per 1 part by weight of drug. 4.The pharmaceutical composition of any one of claims 1 through 3, whereinthe acidic substance is one where when 1 g of said substance isdissolved in 50 ml water, pH of said solution is brought to 6 or lower.5. The pharmaceutical composition of any one of claims 1 through 4,wherein the amount of acidic substance added is the amount that willneutralize 10% or more of basic groups of aminoalkyl methacrylatecopolymer E.
 6. The pharmaceutical composition of any one of claims 1through 5, comprising 0.05˜500 parts by weight of aminoalkylmethacrylate copolymer E per 1 part by weight of drug in the effectiveamount for treatment or prevention of disease, and acidic substance inan amount that will neutralize 10% or more of the basic groups of theabove-mentioned polymer.
 7. The pharmaceutical composition of any one ofclaims 1 through 5, comprising 0.05˜500 parts by weight of aminoalkylmethacrylate copolymer E per 1 part by weight of drug in the effectiveamount for treatment or prevention of disease, and 0.005˜50 parts byweight of acidic substance per 1 part by weight of the above-mentionedpolymer.
 8. The pharmaceutical composition of any one of claims 1through 7, wherein the aminoalkyl methacrylate copolymer E and acidicsubstance are granulated.
 9. The pharmaceutical composition of any oneof claims 1 through 7, wherein the aminoalkyl methacrylate copolymer Eand acidic substance are dissolved in a pharmaceutically acceptablesolvent and/or after dissolution, said substance is spray dried toobtain a spray-dried substance, or said solution is lyophilized toobtain a lyophilized substance.
 10. The pharmaceutical composition ofany one of claims 1 through 7, wherein the aminoalkyl methacrylatecopolymer E and acidic substance are in a state of dissolution and/orsuspension in a pharmaceutically acceptable solvent.
 11. Thepharmaceutical composition of any one of claims 1 through 10, whereinthe form of the pharmaceutical preparation is 1 or 2 or more selectedfrom the group consisting of granules, tablets, capsules, and liquid.12. The pharmaceutical composition of any one of claims 1 through 11,wherein the drug is a drug that is difficult to absorb.
 13. Thepharmaceutical composition of claim 12, wherein the drug is abisphosphonate compound.
 14. A method of improving oral absorption of adrug by using a pharmaceutical composition obtained by bringing drug,aminoalkyl methacrylate copolymer E, and acidic substance together anduniformly mixing at least the above-mentioned polymer and acidicsubstance.
 15. The method of claim 14, wherein a pharmaceuticalcomposition obtained by uniformly mixing drug, aminoalkyl methacrylatecopolymer E, and acidic substance is used.
 16. The method of claim 14 or15, wherein the aminoalkyl methacrylate copolymer E is used in an amountof 0.01 parts by weight or more per 1 part by weight of drug.
 17. Themethod of any one of claims 14 through 16, wherein the acidic. substancethat is used is one with which when 1 g of said substance is dissolvedin 50 ml water, pH of said solution is brought to 6 or lower.
 18. Themethod of any one of claims 14 through 17, wherein the acidic substanceis used in the amount that will neutralize 10% or more of the basicgroups of aminoalkyl methacrylate copolymer E.
 19. The method of any oneof claims 14 through 18, wherein pharmaceutical composition is usedwhich comprises 0.05˜500 parts by weight of aminoalkyl methacrylatecopolymer E in terms of 1 part by weight drug in the amount effective totreat or prevent disease, and acidic substance in an amount that willneutralize 10% or more of basic groups of the above-mentioned polymer.20. The method of any one of claims 14 through 18, wherein apharmaceutical composition is used which comprises 0.05˜500 parts byweight of aminoalkyl methacrylate copolymer E per 1 part by weight ofdrug in an effective amount for treatment or prevention of disease, and0.005˜50 parts by weight of acidic substance per 1 part by weight of theabove-mentioned polymer.
 21. The method of any one of claims 14 through20, wherein a composition is used where the aminoalkyl methacrylatecopolymer E and acidic substance are granulated.
 22. The method of anyone of claims 14 through 20, wherein the aminoalkyl methacrylatecopolymer E and acidic substance are dissolved in a pharmaceuticallyacceptable solvent and/or used as a spray-dried substance that has beenobtained by spray drying said solution or used as a lyophilizedsubstance that has been obtained by lyophilization of said solution. 23.The method of any one of claims 14 through 20, wherein the aminoalkylmethacrylate copolymer E and acidic substance is used in a state ofdissolution and/or suspension in a pharmaceutically acceptable solvent.24. The method of any one of claims 14 through 23, wherein the form ofthe pharmaceutical preparation is 1 or 2 or more selected from the groupconsisting of granules, tablets, capsules, and liquid.
 25. The method ofany one of claims 14 through 24, wherein drug that is difficult toabsorb is used as the drug.
 26. The method of claim 25, wherein abisphosphonate compound is used as the drug.
 27. An agent for improvingoral absorption by increasing drug permeability of the digestive tractmucous membrane and/or the mucus layer distributed over this mucousmembrane, whose active ingredient is aminoalkyl methacrylate copolymerE.
 28. The agent for improving oral absorption of claim 27 by the effectof inhibiting the formation and/or the effect of delaying the formationof slightly soluble complex based on interaction between the drug andthe digestive tract mucous layer and/or digestive tract mucous membrane.29. The agent that promotes oral absorption of claim 27 or 28, which isused in the presence of acidic substance.
 30. The use of aminoalkylmethacrylate copolymer E as an agent for improving oral absorption thatincreases drug permeability of the digestive tract mucous membraneand/or mucus layer distributed over this mucous membrane.
 31. The use ofclaim 30, wherein aminoalkyl methacrylate copolymer .E is used as anagent for improving oral absorption having the effect of inhibiting theformation and/or the effect of delaying the formation of a slightlysoluble complex based on the interaction between a drug and thedigestive tract mucus layer and/or digestive tract mucous membrane. 32.The use of claim 31, which is used in the presence of an acidicsubstance.